IN-SITU SCANNING ACOUSTIC MICROSCOPY OF CRACK BRIDGING IN ALUMINA

IN-SITU SCANNING ACOUSTIC MICROSCOPY OF CRACK BRIDGING IN ALUMINA

High-resolution scanning acoustic microscopy has been used to observe crack bridging in a fine-grained polycrystalline alumina. The microscope is sensitive to the increased acoustic transmission across the crack from the interlocking and sliding asperities that cause crack shielding and -curve behav...

Volledige beschrijving

Bibliografische gegevens
Hoofdauteurs:	Marrow, T, Briggs, G, Roberts, S
Formaat:	Journal article
Gepubliceerd in:	1994

Gelijkaardige items

SCANNING ACOUSTIC MICROSCOPY OBSERVATIONS OF HIGH-TEMPERATURE CRACK-BRIDGING MECHANISMS IN ALUMINA
door: Marrow, J, et al.
Gepubliceerd in: (1993)

EXAMINATION OF CRACKS AND OTHER DEFECTS IN SODIUM BETA-ALUMINA AND BETA''-ALUMINA USING ACOUSTIC, OPTICAL AND ELECTRON-MICROSCOPY
door: Petford, A, et al.
Gepubliceerd in: (1983)

SCANNING ELECTRON ACOUSTIC MICROSCOPY AND SCANNING ACOUSTIC MICROSCOPY - A FAVORABLE COMPARISON
door: Briggs, G
Gepubliceerd in: (1984)

In-situ observation and modelling of intergranular cracking in polycrystalline alumina
door: Marrow, T, et al.
Gepubliceerd in: (2011)

3-DIMENSIONAL MEASUREMENT OF SHORT FATIGUE CRACKS USING SCANNING ACOUSTIC MICROSCOPY
door: Knauss, D, et al.
Gepubliceerd in: (1993)

ACOUSTIC MICROSCOPY OF SURFACE CRACKS
door: Rowe, J, et al.
Gepubliceerd in: (1986)

An introduction to Scanning acoustic microscopy /
door: 190653 Briggs, Andrew
Gepubliceerd in: (1985)

TIME-RESOLVED ACOUSTIC MICROSCOPY OF SHORT CRACKS
door: Knauss, D, et al.
Gepubliceerd in: (1993)

SUBSURFACE CRACK SIGNALS IN TIME-RESOLVED ACOUSTIC MICROSCOPY
door: Knauss, D, et al.
Gepubliceerd in: (1994)

CRACK DETECTION IN SILICON-NITRIDE BY ACOUSTIC MICROSCOPY
door: Lawrence, C, et al.
Gepubliceerd in: (1990)

In-situ study of acoustomigration by scanning acoustic force microscopy
door: Hesjedal, T, et al.
Gepubliceerd in: (2003)

In situ quantitative three-dimensional characterisation of sub-indentation cracking in polycrystalline alumina
door: Vertyagina, Y, et al.
Gepubliceerd in: (2014)

In situ quantitative three-dimensional characterisation of sub-indentation cracking in polycrystalline alumina
door: Vertyagina, Y, et al.
Gepubliceerd in: (2014)

How to measure small cracks by nanosecond acoustic microscopy
door: Briggs, G, et al.
Gepubliceerd in: (1999)

Intergranular crack nucleation in polycrystalline alumina
door: Aswad, M, et al.
Gepubliceerd in: (2010)

Intergranular crack nuclei in polycrystalline alumina
door: Aswad, M, et al.
Gepubliceerd in: (2012)

Intergranular crack nucleation in polycrystalline alumina
door: Aswad, M, et al.
Gepubliceerd in: (2010)

Intergranular crack nuclei in polycrystalline alumina
door: Aswad, M, et al.
Gepubliceerd in: (2012)

Acoustic emission and crack propagation in polycrystalline alumina /
door: Evans, Anthony G. (Anthony Glyn), 1942-

Studies of adhesion and disbonding of coatings by scanning acoustic microscopy
door: Crossen, J, et al.
Gepubliceerd in: (1996)

DEPTH MEASUREMENTS OF SHORT CRACKS IN PERSPEX WITH THE SCANNING ACOUSTIC MICROSCOPE
door: Zhai, T, et al.
Gepubliceerd in: (1993)

DEPTH MEASUREMENTS OF SHORT CRACKS IN PERSPEX WITH THE SCANNING ACOUSTIC MICROSCOPE
door: Zhai, T, et al.
Gepubliceerd in: (1993)

ACOUSTIC MICROSCOPY
door: Briggs, G
Gepubliceerd in: (1988)

IMAGE-PROCESSING FOR THE MEASUREMENT OF CRACK DEPTH USING THE SCANNING ACOUSTIC MICROSCOPE
door: Bennink, D, et al.
Gepubliceerd in: (1993)

Acoustic scanning probe microscopy /
door: Marinello, Francesco, et al.
Gepubliceerd in: (2012)

MIXED-MODE CRACK MOUTH REFLECTION IN TIME-RESOLVED ACOUSTIC MICROSCOPY OF SHORT FATIGUE CRACKS IN SINGLE-CRYSTAL ALUMINUM
door: Zhai, T, et al.
Gepubliceerd in: (1994)

ACOUSTIC MICROSCOPY - A SUMMARY
door: Briggs, G
Gepubliceerd in: (1992)

Scanning acoustic microscopy for material evaluation
door: Hyunung Yu
Gepubliceerd in: (2020-11-01)

New techniques for in-situ observations of crack growth behaviour
door: Marrow, T
Gepubliceerd in: (2008)

HOW FINE A SURFACE CRACK CAN YOU SEE IN A SCANNING ACOUSTIC MICROSCOPE
door: Briggs, G, et al.
Gepubliceerd in: (1990)

Gallium nitride surface preparation optimised using in situ scanning tunnelling microscopy
door: Oliver, R, et al.
Gepubliceerd in: (2003)

Gallium nitride surface preparation optimised using in situ scanning tunnelling microscopy
door: Oliver, R, et al.
Gepubliceerd in: (2003)

IN-SITU OBSERVATIONS OF INTERGRANULAR STRESS CORROSION CRACKING
door: Duff, J, et al.
Gepubliceerd in: (2009)

Segmenting hydrogen‐induced cracking defects in steel through scanning acoustic microscopy and deep neural networks
door: Thi Thu Ha Vu, et al.
Gepubliceerd in: (2024-12-01)

ACOUSTIC MICROSCOPY OF ROCKS
door: Rodriguezrey, A, et al.
Gepubliceerd in: (1990)

Acoustic microscopy for imaging and characterization
door: Briggs, G, et al.
Gepubliceerd in: (1996)

Wideband acoustic microscopy of tissue.
door: Daft, C, et al.
Gepubliceerd in: (1989)

ACOUSTIC MICROSCOPY OF DENTAL-TISSUES
door: Briggs, G, et al.
Gepubliceerd in: (1983)

Surface response of a fluid-loaded solid to impulsive line and point forces: Application to scanning acoustic microscopy
door: Every, A, et al.
Gepubliceerd in: (1998)

Transverse surface acoustic wave detection by scanning acoustic force microscopy
door: Behme, G, et al.
Gepubliceerd in: (1998)