Effects of orientation, stress and exposure time on short intergranular stress corrosion crack behaviour in sensitised type 304 austenitic stainless steel
Intergranular stress corrosion cracking (IGSCC) in austenitic stainless steels occurs at susceptible grain boundaries after sensitisation. In this study, the effects of test duration, static stress (applied and residual) and microstructure orientation on the developed populations of short crack nucl...