Synchrotron X-ray scattering analysis of nylon-12 crystallisation variation depending on 3D printing conditions
Nylon-12 is an important structural polymer in wide use in the form of fibres and bulk structures. Fused filament fabrication (FFF) is an extrusion-based additive manufacturing (AM) method for rapid prototyping and final product manufacturing of thermoplastic polymer objects. The resultant microstru...
| Những tác giả chính: | , , , , , , |
|---|---|
| Định dạng: | Journal article |
| Ngôn ngữ: | English |
| Được phát hành: |
MDPI
2020
|
| Tóm tắt: | Nylon-12 is an important structural polymer in wide use in the form of fibres and bulk structures. Fused filament fabrication (FFF) is an extrusion-based additive manufacturing (AM) method for rapid prototyping and final product manufacturing of thermoplastic polymer objects. The resultant microstructure of FFF-produced samples is strongly affected by the cooling rates and thermal gradients experienced across the part. The crystallisation behaviour during cooling and solidification influences the micro- and nano-structure, and deserves detailed investigation. A commercial Nylon-12 filament and FFF-produced Nylon-12 parts were studied by differential scanning calorimetry (DSC) and wide-angle X-ray scattering (WAXS) to examine the effect of cooling rates under non-isothermal crystallisation conditions on the microstructure and properties. Slower cooling rates caused more perfect crystallite formation, as well as alteration to the thermal properties. |
|---|