Digital image correlation has been applied to optical images in order to detect crack nuclei in fine-grain size pure and Cr-doped aluminas. Individual intergranular crack nuclei within areas comprising tens of thousands of grains were detectable, and their crack lengths and opening strains obtained...

Полное описание

Библиографические подробности
Главные авторы:	Aswad, M, Marrow, T
Формат:	Journal article
Язык:	English
Опубликовано:	Elsevier 2012

Схожие документы

Intergranular crack nuclei in polycrystalline alumina
по: Aswad, M, и др.
Опубликовано: (2012)

Intergranular crack nucleation in polycrystalline alumina
по: Aswad, M, и др.
Опубликовано: (2010)

Intergranular crack nucleation in polycrystalline alumina
по: Aswad, M, и др.
Опубликовано: (2010)

In-situ observation and modelling of intergranular cracking in polycrystalline alumina
по: Marrow, T, и др.
Опубликовано: (2011)

IN-SITU OBSERVATIONS OF INTERGRANULAR STRESS CORROSION CRACKING
по: Duff, J, и др.
Опубликовано: (2009)

In situ quantitative three-dimensional characterisation of sub-indentation cracking in polycrystalline alumina
по: Vertyagina, Y, и др.
Опубликовано: (2014)

In situ quantitative three-dimensional characterisation of sub-indentation cracking in polycrystalline alumina
по: Vertyagina, Y, и др.
Опубликовано: (2014)

Direct observations of electrochemically induced intergranular cracking in polycrystalline NMC811 particles
по: Parks, HCW, и др.
Опубликовано: (2022)

A three-dimensional computational model for intergranular cracking
по: Jivkov, A, и др.
Опубликовано: (2006)

The roles of microstructure and mechanics in intergranular stress corrosion cracking
по: Jivkov, A, и др.
Опубликовано: (2005)

Acoustic emission and crack propagation in polycrystalline alumina /
по: Evans, Anthony G. (Anthony Glyn), 1942-

Diffraction contrast tomography of polycrystalline alumina
по: Marrow, T, и др.
Опубликовано: (2009)

3D modelling of intergranular stress corrosion cracking (IGSCC)
по: Zhang, Y, и др.
Опубликовано: (2009)

3D modelling of intergranular stress corrosion cracking (IGSCC)
по: Zhang, Y, и др.
Опубликовано: (2009)

Rates of intergranular environment assisted cracking in three-dimensional model microstructures
по: Jivkov, A, и др.
Опубликовано: (2007)

New techniques for intergranular stress corrosion crack observation
по: Marrow, T, и др.
Опубликовано: (2008)

Modelling intergranular stress corrosion cracking in simulated three-dimensional microstructures
по: Jivkov, A, и др.
Опубликовано: (2007)

Detection and characterisation of intergranular stress-corrosion cracking on austenitic stainless steel
по: Kovac, J, и др.
Опубликовано: (2012)

A two-dimensional mesoscale model for intergranular stress corrosion crack propagation
по: Jivkov, A, и др.
Опубликовано: (2006)

Mesoscale mechanical model for intergranular stress corrosion cracking and implications for microstructure engineering
по: Jivkov, A, и др.
Опубликовано: (2008)

Mesoscale mechanical model for intergranular stress corrosion cracking and implications for microstructure engineering
по: Jivkov, A, и др.
Опубликовано: (2008)

A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
по: Rahimi, S, и др.
Опубликовано: (2019)

Observations of intergranular stress corrosion cracking in a grain-mapped polycrystal.
по: King, A, и др.
Опубликовано: (2008)

Grain boundary engineering for crack bridging: A new model for intergranular stress corrosion crack (IGSCC) propagation
по: Engelberg, D, и др.
Опубликовано: (2008)

A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
по: S. Rahimi, и др.
Опубликовано: (2020-02-01)

Numerical modelling of intergranular fracture in polycrystalline materials and grain size effects
по: P. Wriggers, и др.
Опубликовано: (2011-07-01)

Numerical modelling of intergranular fracture in polycrystalline materials and grain size effects
по: M. Paggi, и др.
Опубликовано: (2013-04-01)

Numerical modelling of intergranular fracture in polycrystalline materials and grain size effects
по: M. Paggi, и др.
Опубликовано: (2013-04-01)

Intergranular stresses in polycrystalline fatigue: diffraction measurement and self-consistent modelling
по: Korsunsky, A, и др.
Опубликовано: (2003)

Influence of microstructure and stress on short intergranular stress corrosion crack growth in austenitic stainless steel type 304
по: Rahimi, S, и др.
Опубликовано: (2008)

In situ observation of intergranular crack nucleation in a grain boundary controlled austenitic stainless steel.
по: Rahimi, S, и др.
Опубликовано: (2009)

In situ observation of intergranular crack nucleation in a grain boundary controlled austenitic stainless steel.
по: Rahimi, S, и др.
Опубликовано: (2009)

Intergranular stresses in polycrystalline fatigue: diffraction measurement and self-consistent modelling
по: Korsunsky, A, и др.
Опубликовано: (2004)

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
по: Babout, L, и др.
Опубликовано: (2006)

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
по: Babout, L, и др.
Опубликовано: (2006)

Three-dimensional observation and image-based modelling of thermal strains in polycrystalline alumina
по: Gonzalez, D, и др.
Опубликовано: (2013)

Cracks in refractory concrete: Transgranular or intergranular?
по: Christian Jung, и др.
Опубликовано: (2025-02-01)

Adaptive 3D algorithm to detect bridging ligaments during intergranular stress corrosion cracking of stainless steel
по: Janaszewski, M, и др.
Опубликовано: (2007)

Towards modelling intergranular stress-corrosion cracks using experimentally obtained grain topologies
по: Simonovski, I, и др.
Опубликовано: (2010)

Effect of surface machining on intergranular stress corrosion cracking (IGSCC) in sensitised type 304 austenitic stainless steel
по: Rahimi, S, и др.
Опубликовано: (2016)