Intergranular crack nuclei in polycrystalline alumina

Intergranular crack nuclei in polycrystalline alumina

Hiển thị phiên bản (1) khác

Digital image correlation has been applied to optical images in order to detect crack nuclei in fine-grain size pure and Cr-doped aluminas. Individual intergranular crack nuclei within areas comprising tens of thousands of grains were detectable, and their crack lengths and opening strains obtained...

Mô tả đầy đủ

Chi tiết về thư mục
Những tác giả chính:	Aswad, M, Marrow, T
Định dạng:	Journal article
Ngôn ngữ:	English
Được phát hành:	Elsevier 2012

Những quyển sách tương tự

Intergranular crack nuclei in polycrystalline alumina
Bằng: Aswad, M, et al.
Được phát hành: (2012)

Intergranular crack nucleation in polycrystalline alumina
Bằng: Aswad, M, et al.
Được phát hành: (2010)

Intergranular crack nucleation in polycrystalline alumina
Bằng: Aswad, M, et al.
Được phát hành: (2010)

In-situ observation and modelling of intergranular cracking in polycrystalline alumina
Bằng: Marrow, T, et al.
Được phát hành: (2011)

IN-SITU OBSERVATIONS OF INTERGRANULAR STRESS CORROSION CRACKING
Bằng: Duff, J, et al.
Được phát hành: (2009)

In situ quantitative three-dimensional characterisation of sub-indentation cracking in polycrystalline alumina
Bằng: Vertyagina, Y, et al.
Được phát hành: (2014)

In situ quantitative three-dimensional characterisation of sub-indentation cracking in polycrystalline alumina
Bằng: Vertyagina, Y, et al.
Được phát hành: (2014)

Direct observations of electrochemically induced intergranular cracking in polycrystalline NMC811 particles
Bằng: Parks, HCW, et al.
Được phát hành: (2022)

A three-dimensional computational model for intergranular cracking
Bằng: Jivkov, A, et al.
Được phát hành: (2006)

The roles of microstructure and mechanics in intergranular stress corrosion cracking
Bằng: Jivkov, A, et al.
Được phát hành: (2005)

Acoustic emission and crack propagation in polycrystalline alumina /
Bằng: Evans, Anthony G. (Anthony Glyn), 1942-

Diffraction contrast tomography of polycrystalline alumina
Bằng: Marrow, T, et al.
Được phát hành: (2009)

3D modelling of intergranular stress corrosion cracking (IGSCC)
Bằng: Zhang, Y, et al.
Được phát hành: (2009)

3D modelling of intergranular stress corrosion cracking (IGSCC)
Bằng: Zhang, Y, et al.
Được phát hành: (2009)

Rates of intergranular environment assisted cracking in three-dimensional model microstructures
Bằng: Jivkov, A, et al.
Được phát hành: (2007)

New techniques for intergranular stress corrosion crack observation
Bằng: Marrow, T, et al.
Được phát hành: (2008)

Modelling intergranular stress corrosion cracking in simulated three-dimensional microstructures
Bằng: Jivkov, A, et al.
Được phát hành: (2007)

Detection and characterisation of intergranular stress-corrosion cracking on austenitic stainless steel
Bằng: Kovac, J, et al.
Được phát hành: (2012)

A two-dimensional mesoscale model for intergranular stress corrosion crack propagation
Bằng: Jivkov, A, et al.
Được phát hành: (2006)

Mesoscale mechanical model for intergranular stress corrosion cracking and implications for microstructure engineering
Bằng: Jivkov, A, et al.
Được phát hành: (2008)

Mesoscale mechanical model for intergranular stress corrosion cracking and implications for microstructure engineering
Bằng: Jivkov, A, et al.
Được phát hành: (2008)

A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
Bằng: Rahimi, S, et al.
Được phát hành: (2019)

Observations of intergranular stress corrosion cracking in a grain-mapped polycrystal.
Bằng: King, A, et al.
Được phát hành: (2008)

Grain boundary engineering for crack bridging: A new model for intergranular stress corrosion crack (IGSCC) propagation
Bằng: Engelberg, D, et al.
Được phát hành: (2008)

A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
Bằng: S. Rahimi, et al.
Được phát hành: (2020-02-01)

Numerical modelling of intergranular fracture in polycrystalline materials and grain size effects
Bằng: P. Wriggers, et al.
Được phát hành: (2011-07-01)

Numerical modelling of intergranular fracture in polycrystalline materials and grain size effects
Bằng: M. Paggi, et al.
Được phát hành: (2013-04-01)

Numerical modelling of intergranular fracture in polycrystalline materials and grain size effects
Bằng: M. Paggi, et al.
Được phát hành: (2013-04-01)

Intergranular stresses in polycrystalline fatigue: diffraction measurement and self-consistent modelling
Bằng: Korsunsky, A, et al.
Được phát hành: (2003)

Influence of microstructure and stress on short intergranular stress corrosion crack growth in austenitic stainless steel type 304
Bằng: Rahimi, S, et al.
Được phát hành: (2008)

In situ observation of intergranular crack nucleation in a grain boundary controlled austenitic stainless steel.
Bằng: Rahimi, S, et al.
Được phát hành: (2009)

In situ observation of intergranular crack nucleation in a grain boundary controlled austenitic stainless steel.
Bằng: Rahimi, S, et al.
Được phát hành: (2009)

Intergranular stresses in polycrystalline fatigue: diffraction measurement and self-consistent modelling
Bằng: Korsunsky, A, et al.
Được phát hành: (2004)

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
Bằng: Babout, L, et al.
Được phát hành: (2006)

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
Bằng: Babout, L, et al.
Được phát hành: (2006)

Three-dimensional observation and image-based modelling of thermal strains in polycrystalline alumina
Bằng: Gonzalez, D, et al.
Được phát hành: (2013)

Cracks in refractory concrete: Transgranular or intergranular?
Bằng: Christian Jung, et al.
Được phát hành: (2025-02-01)

Adaptive 3D algorithm to detect bridging ligaments during intergranular stress corrosion cracking of stainless steel
Bằng: Janaszewski, M, et al.
Được phát hành: (2007)

Towards modelling intergranular stress-corrosion cracks using experimentally obtained grain topologies
Bằng: Simonovski, I, et al.
Được phát hành: (2010)

Effect of surface machining on intergranular stress corrosion cracking (IGSCC) in sensitised type 304 austenitic stainless steel
Bằng: Rahimi, S, et al.
Được phát hành: (2016)