Three-dimensional characterization of stress corrosion cracks

Three-dimensional characterization of stress corrosion cracks

Mostra altre versioni (1)

Understanding crack propagation and initiation is fundamental if stress corrosion cracking (SCC) mechanisms are to be understood. However, cracking is a three-dimensional (3D) phenomenon and most characterization techniques are restricted to two-dimensional (2D) observations. In order to overcome th...

Descrizione completa

Dettagli Bibliografici
Autori principali:	Lozano-Perez, S, Rodrigo, P, Gontard, L
Natura:	Journal article
Lingua:	English
Pubblicazione:	2011

Documenti analoghi

Three-dimensional characterization of stress corrosion cracks
di: Lozano-Perez, S, et al.
Pubblicazione: (2011)

Understanding stress corrosion cracking with electron tomography
di: Lozano-Perez, S, et al.
Pubblicazione: (2008)

Novel characterization of stress corrosion cracks
di: Lozano-Perez, S
Pubblicazione: (2008)

Novel characterization of stress corrosion cracks
di: Lozano-Perez, S
Pubblicazione: (2008)

TEM characterization of stress corrosion cracks in 304SS
di: Lozano-Perez, S, et al.
Pubblicazione: (2004)

TEM characterization of stress corrosion cracks in 304SS
di: Lozano-Perez, S, et al.
Pubblicazione: (2004)

Modelling intergranular stress corrosion cracking in simulated three-dimensional microstructures
di: Jivkov, A, et al.
Pubblicazione: (2007)

Three dimensional observations and modelling of intergranular stress corrosion cracking in austenitic stainless steel
di: Marrow, T, et al.
Pubblicazione: (2006)

A multi-scale approach to stress corrosion cracking
di: Lozano-Perez, S, et al.
Pubblicazione: (2008)

A multi-scale approach to stress corrosion cracking
di: Lozano-Perez, S, et al.
Pubblicazione: (2008)

A study on the diffusion-induced grain boundary migration ahead of stress corrosion cracking crack tips through advanced characterization
di: Shen, Z, et al.
Pubblicazione: (2021)

3D ATOM-PROBE CHARACTERIZATION OF STRESS AND COLD-WORK IN STRESS CORROSION CRACKING OF 304 STAINLESS STEEL
di: Kruska, K, et al.
Pubblicazione: (2011)

3D ATOM-PROBE CHARACTERIZATION OF STRESS AND COLD-WORK IN STRESS CORROSION CRACKING OF 304 STAINLESS STEEL
di: Kruska, K, et al.
Pubblicazione: (2011)

Characterization Of Strain Hardening Three Dimensional Crack-Tip Stress Field
di: Zakaria, Muhammad Naim
Pubblicazione: (2022)

Microstructural characterization of intergranular stress corrosion cracking of 300 series stainless steels in PWR conditions
di: Huang, Y, et al.
Pubblicazione: (2001)

Characterization of Corrosion and Stress Corrosion Cracking of AE44 Magnesium Alloy
di: M. Sozańska, et al.
Pubblicazione: (2020-03-01)

Stress-corrosion cracking /
di: Jones, Russell H.
Pubblicazione: (1992)

TEM investigations of intergranular stress corrosion cracking in austenitic alloys in PWR environmental conditions
di: Lozano-Perez, S, et al.
Pubblicazione: (2003)

TEM investigations of intergranular stress corrosion cracking in austenitic alloys in PWR environmental conditions
di: Lozano-Perez, S, et al.
Pubblicazione: (2003)

Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content
di: Lozano-Perez, S, et al.
Pubblicazione: (2009)

Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content
di: Lozano-Perez, S, et al.
Pubblicazione: (2009)

Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content
di: Lozano-Perez, S, et al.
Pubblicazione: (2009)

Stress corrosion cracking of pipelines /
di: Cheng, Y. Frank, 1969-
Pubblicazione: (2013)

Stress corrosion cracking of steels/
di: 287285 Karpenko, G. V., et al.
Pubblicazione: (1979)

Atom probe tomography of stress corrosion crack tips in SUS316 stainless steels
di: Meisnar, M, et al.
Pubblicazione: (2015)

A two-dimensional mesoscale model for intergranular stress corrosion crack propagation
di: Jivkov, A, et al.
Pubblicazione: (2006)

A guide on FIB preparation of samples containing stress corrosion crack tips for TEM and atom-probe analysis.
di: Lozano-Perez, S
Pubblicazione: (2008)

Crack Growth Rate Analysis of Stress Corrosion Cracking
di: Mohamed Alkateb, et al.
Pubblicazione: (2021-01-01)

A guide on FIB preparation of samples containing stress corrosion crack tips for TEM and atom-probe analysis
di: Lozano-Perez, S
Pubblicazione: (2008)

Preparation of TEM specimens containing stress corrosion cracks in austenitic alloys using FIB
di: Lozano-Perez, S, et al.
Pubblicazione: (2001)

Characterization of elastic strain field and geometrically necessary dislocation distribution in stress corrosion cracking of 316 stainless steels by transmission Kikuchi diffraction
di: Wilkinson, A, et al.
Pubblicazione: (2015)

Dynamical observations on the crack tip zone and stress corrosion of two-dimensional MoS2
di: Thuc Hue Ly, et al.
Pubblicazione: (2017-01-01)

Stress corrosion cracking : theory and practice /
di: Raja, V. S., et al.
Pubblicazione: (2011)

Three-Dimensional Elastic-Plastic Crack Tip Stress Fields
di: Mohd Nor Halimuddin, Normalyana
Pubblicazione: (2022)

Micromechanical testing of stress corrosion cracking
di: Herbert, F, et al.
Pubblicazione: (2010)

Understanding the mechanisms of stress corrosion cracking
di: Kruska, K
Pubblicazione: (2012)

COMPOSITION, MICROSTRUCTURE, AND STRESS-CORROSION CRACKING
di: Sykes, J
Pubblicazione: (1993)

Stress corrosion cracking test methods /
di: Sedriks, A. John, author, et al.
Pubblicazione: (1990)

Stress corrosion cracking of aluminium alloys /
di: 333484 Jainal Bonandar
Pubblicazione: (1986)

Stress-corrosion cracking and hydrogen embrittlement
di: British Ship Research Association
Pubblicazione: ([n d)