Three-dimensional characterization of stress corrosion cracks
Understanding crack propagation and initiation is fundamental if stress corrosion cracking (SCC) mechanisms are to be understood. However, cracking is a three-dimensional (3D) phenomenon and most characterization techniques are restricted to two-dimensional (2D) observations. In order to overcome th...
Principais autores: | Lozano-Perez, S, Rodrigo, P, Gontard, L |
---|---|
Formato: | Journal article |
Idioma: | English |
Publicado em: |
2011
|
Registros relacionados
-
Three-dimensional characterization of stress corrosion cracks
por: Lozano-Perez, S, et al.
Publicado em: (2011) -
Understanding stress corrosion cracking with electron tomography
por: Lozano-Perez, S, et al.
Publicado em: (2008) -
Novel characterization of stress corrosion cracks
por: Lozano-Perez, S
Publicado em: (2008) -
Novel characterization of stress corrosion cracks
por: Lozano-Perez, S
Publicado em: (2008) -
TEM characterization of stress corrosion cracks in 304SS
por: Lozano-Perez, S, et al.
Publicado em: (2004)