X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel

عرض إصدارات أخرى (1)

Intergranular stress corrosion cracking in a sensitised type 302 stainless steel wire has been observed in situ using high resolution X-ray microtomography. Tomography enables the development and failure of crack bridging ligaments to be studied in detail in three dimensions. Direct comparison of th...

وصف كامل

التفاصيل البيبلوغرافية
المؤلفون الرئيسيون:	Babout, L, Marrow, T, Engelberg, D, Withers, P
التنسيق:	Conference item
منشور في:	2006

مواد مشابهة

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
حسب: Babout, L, وآخرون
منشور في: (2006)

Intergranular stress corrosion crack propagation in sensitised austenitic stainless steel (microstructure modelling and experimental observation)
حسب: Marrow, T, وآخرون
منشور في: (2006)

Three dimensional observations and modelling of intergranular stress corrosion cracking in austenitic stainless steel
حسب: Marrow, T, وآخرون
منشور في: (2006)

Effect of surface machining on intergranular stress corrosion cracking (IGSCC) in sensitised type 304 austenitic stainless steel
حسب: Rahimi, S, وآخرون
منشور في: (2016)

Effects of orientation, stress and exposure time on short intergranular stress corrosion crack behaviour in sensitised type 304 austenitic stainless steel
حسب: Rahimi, S, وآخرون
منشور في: (2012)

Effects of orientation, stress and exposure time on short intergranular stress corrosion crack behaviour in sensitised type 304 austenitic stainless steel
حسب: Rahimi, S, وآخرون
منشور في: (2012)

Detection and characterisation of intergranular stress-corrosion cracking on austenitic stainless steel
حسب: Kovac, J, وآخرون
منشور في: (2012)

In situ observation of intergranular crack nucleation in a grain boundary controlled austenitic stainless steel.
حسب: Rahimi, S, وآخرون
منشور في: (2009)

In situ observation of intergranular crack nucleation in a grain boundary controlled austenitic stainless steel.
حسب: Rahimi, S, وآخرون
منشور في: (2009)

Grain boundary structure and intergranular stress corrosion crack initiation in high temperature water of a thermally sensitised austenitic stainless steel, observed in situ
حسب: Stratulat, A, وآخرون
منشور في: (2014)

Grain boundary structure and intergranular stress corrosion crack initiation in high temperature water of a thermally sensitised austenitic stainless steel, observed in situ
حسب: Stratulat, A, وآخرون
منشور في: (2014)

A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
حسب: Rahimi, S, وآخرون
منشور في: (2019)

A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
حسب: S. Rahimi, وآخرون
منشور في: (2020-02-01)

Adaptive 3D algorithm to detect bridging ligaments during intergranular stress corrosion cracking of stainless steel
حسب: Janaszewski, M, وآخرون
منشور في: (2007)

Influence of microstructure and stress on short intergranular stress corrosion crack growth in austenitic stainless steel type 304
حسب: Rahimi, S, وآخرون
منشور في: (2008)

Effect of strain path and annealing on development of resistance to intergranular degradation in austenitic stainless steels
حسب: Randle, V, وآخرون
منشور في: (2008)

Mechanical criterion for nucleation of intergranular stress corrosion cracking in austenitic stainless steel
حسب: Tomoyuki Fujii, وآخرون
منشور في: (2021-09-01)

Correlations of electrochemical noise, acoustic emission and complementary monitoring techniques during intergranular stress-corrosion cracking of austenitic stainless steel
حسب: Kovac, J, وآخرون
منشور في: (2010)

Influence of milling on the development of stress corrosion cracks in austenitic stainless steel
حسب: Lyon, K, وآخرون
منشور في: (2014)

New techniques for intergranular stress corrosion crack observation
حسب: Marrow, T, وآخرون
منشور في: (2008)

Nonlinear Ultrasonic Characterization for Intergranular Corrosion Susceptibility of 304 Austenitic Stainless Steel
حسب: HOU Tian-yu, وآخرون
منشور في: (2017-10-01)

Electrochemical Analysis on Intergranular Corrosion of Austenitic Stainless Steel Weld in Molten Nitrate Salt
حسب: Noparat Kanjanaprayut, وآخرون
منشور في: (2024-11-01)

Microstructures and intergranular corrosion resistances of hot-rolled austenitic stainless steel clad plates
حسب: Ju-Chan Jin, وآخرون
منشور في: (2023-09-01)

Observations of intergranular stress corrosion cracking in a grain-mapped polycrystal.
حسب: King, A, وآخرون
منشور في: (2008)

Characterisation of grain boundary cluster compactness in austenitic stainless steel
حسب: Rahimi, S, وآخرون
منشور في: (2010)

Grain boundary engineering for crack bridging: A new model for intergranular stress corrosion crack (IGSCC) propagation
حسب: Engelberg, D, وآخرون
منشور في: (2008)

IN-SITU OBSERVATIONS OF INTERGRANULAR STRESS CORROSION CRACKING
حسب: Duff, J, وآخرون
منشور في: (2009)

Overview of Intergranular Fracture of Neutron Irradiated Austenitic Stainless Steels
حسب: Anna Hojná
منشور في: (2017-09-01)

Intergranular Corrosion Analysis of Austenitic Stainless Steels in Molten Nitrate Salt Using Electrochemical Characterization
حسب: Noparat Kanjanaprayut, وآخرون
منشور في: (2024-01-01)

Towards Understanding the Development of Grain Boundary Clusters in Austenitic Stainless Steel
حسب: Engelberg, D, وآخرون
منشور في: (2010)

Diffraction contrast tomography for the study of polycrystalline stainless steel microstructures and stress corrosion cracking
حسب: King, A, وآخرون
منشور في: (2011)

Effect of thermomechanical process history on grain boundary control in an austenitic stainless steel
حسب: Engelberg, D, وآخرون
منشور في: (2008)

The roles of microstructure and mechanics in intergranular stress corrosion cracking
حسب: Jivkov, A, وآخرون
منشور في: (2005)

The stress corrosion of a sensitised stainless steel
حسب: Moss, C, وآخرون
منشور في: (1989)

Investigation of chloride stress corrosion cracking in austenitic stainless steel
حسب: Mohamad Khairuazlan, Kamaruzaman
منشور في: (2013)

New sights on intergranular corrosion resistance mechanism of type 304 austenitic stainless steel by adjusting carbon contents
حسب: Liming Mou, وآخرون
منشور في: (2023-09-01)

Influence of Secondary Phase Precipitation on Resistance to Intergranular Corrosion of AiSi 316l Austenitic Stainless Steel
حسب: Katarina Bartova, وآخرون
منشور في: (2010-12-01)

Thermal Aging Effects on Mechanical and Intergranular Corrosion Resistance of Super-Austenitic Stainless Steel exposed at 600˚C
حسب: A.S.M Cardoso, وآخرون
منشور في: (2022-07-01)

Diagnostics of the effect of prior cold deformation and aging time on intergranular corrosion resistance in case of austenitic stainless steel
حسب: Ławrynowicz Zdzisław
منشور في: (2018-01-01)

A new approach for DL-EPR testing of thermo-mechanically processed austenitic stainless steel
حسب: Rahimi, S, وآخرون
منشور في: (2011)