X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel

Zobrazit další vydání (1)

Intergranular stress corrosion cracking in a sensitised type 302 stainless steel wire has been observed in situ using high resolution X-ray microtomography. Tomography enables the development and failure of crack bridging ligaments to be studied in detail in three dimensions. Direct comparison of th...

Podrobná bibliografie
Hlavní autoři:	Babout, L, Marrow, T, Engelberg, D, Withers, P
Médium:	Conference item
Vydáno:	2006

Podobné jednotky

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
Autor: Babout, L, a další
Vydáno: (2006)

Intergranular stress corrosion crack propagation in sensitised austenitic stainless steel (microstructure modelling and experimental observation)
Autor: Marrow, T, a další
Vydáno: (2006)

Three dimensional observations and modelling of intergranular stress corrosion cracking in austenitic stainless steel
Autor: Marrow, T, a další
Vydáno: (2006)

Effect of surface machining on intergranular stress corrosion cracking (IGSCC) in sensitised type 304 austenitic stainless steel
Autor: Rahimi, S, a další
Vydáno: (2016)

Effects of orientation, stress and exposure time on short intergranular stress corrosion crack behaviour in sensitised type 304 austenitic stainless steel
Autor: Rahimi, S, a další
Vydáno: (2012)

Effects of orientation, stress and exposure time on short intergranular stress corrosion crack behaviour in sensitised type 304 austenitic stainless steel
Autor: Rahimi, S, a další
Vydáno: (2012)

Detection and characterisation of intergranular stress-corrosion cracking on austenitic stainless steel
Autor: Kovac, J, a další
Vydáno: (2012)

In situ observation of intergranular crack nucleation in a grain boundary controlled austenitic stainless steel.
Autor: Rahimi, S, a další
Vydáno: (2009)

In situ observation of intergranular crack nucleation in a grain boundary controlled austenitic stainless steel.
Autor: Rahimi, S, a další
Vydáno: (2009)

Grain boundary structure and intergranular stress corrosion crack initiation in high temperature water of a thermally sensitised austenitic stainless steel, observed in situ
Autor: Stratulat, A, a další
Vydáno: (2014)

Grain boundary structure and intergranular stress corrosion crack initiation in high temperature water of a thermally sensitised austenitic stainless steel, observed in situ
Autor: Stratulat, A, a další
Vydáno: (2014)

A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
Autor: Rahimi, S, a další
Vydáno: (2019)

A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
Autor: S. Rahimi, a další
Vydáno: (2020-02-01)

Adaptive 3D algorithm to detect bridging ligaments during intergranular stress corrosion cracking of stainless steel
Autor: Janaszewski, M, a další
Vydáno: (2007)

Influence of microstructure and stress on short intergranular stress corrosion crack growth in austenitic stainless steel type 304
Autor: Rahimi, S, a další
Vydáno: (2008)

Effect of strain path and annealing on development of resistance to intergranular degradation in austenitic stainless steels
Autor: Randle, V, a další
Vydáno: (2008)

Mechanical criterion for nucleation of intergranular stress corrosion cracking in austenitic stainless steel
Autor: Tomoyuki Fujii, a další
Vydáno: (2021-09-01)

Correlations of electrochemical noise, acoustic emission and complementary monitoring techniques during intergranular stress-corrosion cracking of austenitic stainless steel
Autor: Kovac, J, a další
Vydáno: (2010)

Influence of milling on the development of stress corrosion cracks in austenitic stainless steel
Autor: Lyon, K, a další
Vydáno: (2014)

New techniques for intergranular stress corrosion crack observation
Autor: Marrow, T, a další
Vydáno: (2008)

Nonlinear Ultrasonic Characterization for Intergranular Corrosion Susceptibility of 304 Austenitic Stainless Steel
Autor: HOU Tian-yu, a další
Vydáno: (2017-10-01)

Electrochemical Analysis on Intergranular Corrosion of Austenitic Stainless Steel Weld in Molten Nitrate Salt
Autor: Noparat Kanjanaprayut, a další
Vydáno: (2024-11-01)

Microstructures and intergranular corrosion resistances of hot-rolled austenitic stainless steel clad plates
Autor: Ju-Chan Jin, a další
Vydáno: (2023-09-01)

Observations of intergranular stress corrosion cracking in a grain-mapped polycrystal.
Autor: King, A, a další
Vydáno: (2008)

Characterisation of grain boundary cluster compactness in austenitic stainless steel
Autor: Rahimi, S, a další
Vydáno: (2010)

Grain boundary engineering for crack bridging: A new model for intergranular stress corrosion crack (IGSCC) propagation
Autor: Engelberg, D, a další
Vydáno: (2008)

IN-SITU OBSERVATIONS OF INTERGRANULAR STRESS CORROSION CRACKING
Autor: Duff, J, a další
Vydáno: (2009)

Overview of Intergranular Fracture of Neutron Irradiated Austenitic Stainless Steels
Autor: Anna Hojná
Vydáno: (2017-09-01)

Intergranular Corrosion Analysis of Austenitic Stainless Steels in Molten Nitrate Salt Using Electrochemical Characterization
Autor: Noparat Kanjanaprayut, a další
Vydáno: (2024-01-01)

Towards Understanding the Development of Grain Boundary Clusters in Austenitic Stainless Steel
Autor: Engelberg, D, a další
Vydáno: (2010)

Diffraction contrast tomography for the study of polycrystalline stainless steel microstructures and stress corrosion cracking
Autor: King, A, a další
Vydáno: (2011)

Effect of thermomechanical process history on grain boundary control in an austenitic stainless steel
Autor: Engelberg, D, a další
Vydáno: (2008)

The roles of microstructure and mechanics in intergranular stress corrosion cracking
Autor: Jivkov, A, a další
Vydáno: (2005)

The stress corrosion of a sensitised stainless steel
Autor: Moss, C, a další
Vydáno: (1989)

Investigation of chloride stress corrosion cracking in austenitic stainless steel
Autor: Mohamad Khairuazlan, Kamaruzaman
Vydáno: (2013)

New sights on intergranular corrosion resistance mechanism of type 304 austenitic stainless steel by adjusting carbon contents
Autor: Liming Mou, a další
Vydáno: (2023-09-01)

Influence of Secondary Phase Precipitation on Resistance to Intergranular Corrosion of AiSi 316l Austenitic Stainless Steel
Autor: Katarina Bartova, a další
Vydáno: (2010-12-01)

Thermal Aging Effects on Mechanical and Intergranular Corrosion Resistance of Super-Austenitic Stainless Steel exposed at 600˚C
Autor: A.S.M Cardoso, a další
Vydáno: (2022-07-01)

Diagnostics of the effect of prior cold deformation and aging time on intergranular corrosion resistance in case of austenitic stainless steel
Autor: Ławrynowicz Zdzisław
Vydáno: (2018-01-01)

A new approach for DL-EPR testing of thermo-mechanically processed austenitic stainless steel
Autor: Rahimi, S, a další
Vydáno: (2011)