X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
Intergranular stress corrosion cracking in a sensitised type 302 stainless steel wire has been observed in situ using high resolution X-ray microtomography. Tomography enables the development and failure of crack bridging ligaments to be studied in detail in three dimensions. Direct comparison of th...