Mapping the evolution of density in 3D of thermally oxidised graphite for nuclear applications

Mapping the evolution of density in 3D of thermally oxidised graphite for nuclear applications

This paper deals with the use of X-ray tomography and subsequent kernel operations on the reconstructed images to generate 3D density maps and phase labelling of polygranular graphite subjected to thermal oxidation which, in some respects, simulates radiolytic oxidation. This shows the suitability o...

Fuld beskrivelse

Bibliografiske detaljer
Main Authors:	Babout, L, Marrow, T, Mummery, P, Withers, P
Format:	Journal article
Sprog:	English
Udgivet:	2006

Lignende værker

X-ray tomographic observations applied to porosity models for the thermal properties of oxidised nuclear graphite
af: Babout, L, et al.
Udgivet: (2007)

Three-dimensional characterization and thermal property modelling of thermally oxidized nuclear graphite
af: Babout, L, et al.
Udgivet: (2008)

Failure analysis of the effects of porosity in thermally oxidised nuclear graphite using finite element modelling
af: Berre, C, et al.
Udgivet: (2008)

The effect of thermal oxidation on polycrystalline graphite studied by X-ray tomography
af: Babout, L, et al.
Udgivet: (2005)

Numerical modelling of the effects of porosity changes on the mechanical properties of nuclear graphite
af: Berre, C, et al.
Udgivet: (2006)

A multi-scale three-dimensional Cellular Automata fracture model of radiolytically oxidised nuclear graphite
af: Vertyagina, Y, et al.
Udgivet: (2017)

Fracture behaviour of radiolytically oxidised reactor core graphites: a view
af: Hodgkins, A, et al.
Udgivet: (2010)

Observation of microstructure deformation and damage in nuclear graphite
af: Joyce, MR, et al.
Udgivet: (2008)

Crack propagation resistance and damage mechanisms in nuclear graphite
af: Hodgkins, A, et al.
Udgivet: (2007)

Research activities of the Nuclear Graphite Research Group - University of Manchester
af: Marsden, B, et al.
Udgivet: (2004)

Crack propagation resistance and damage mechanisms in nuclear graphite
af: Hodgkins, A, et al.
Udgivet: (2006)

X-ray tomography observation of crack propagation in nuclear graphite
af: Hodgkins, A, et al.
Udgivet: (2006)

Microstructural modelling of nuclear graphite using multi-phase models
af: Berre, C, et al.
Udgivet: (2008)

Research activities of the Nuclear Graphite Research Group at the University of Manchester, UK
af: Marsden, B, et al.
Udgivet: (2004)

A method for the 3-D quantification of bridging ligaments during crack propagation
af: Babout, L, et al.
Udgivet: (2011)

Assessment of the fracture toughness of neutron-irradiated nuclear graphite by 3D analysis of the crack displacement field
af: Jin, X, et al.
Udgivet: (2020)

Analysis of crack propagation in nuclear graphite using three-point bending of sandwiched specimens
af: Shi, L, et al.
Udgivet: (2004)

Modelling damage in nuclear graphite
af: Becker, T, et al.
Udgivet: (2013)

The microstructure of nuclear graphite binders
af: Wen, K, et al.
Udgivet: (2008)

Nanostructures of carbon in nuclear graphite
af: Wen, K, et al.
Udgivet: (2008)

Nanostructures of carbon in nuclear graphite
af: Wen, K, et al.
Udgivet: (2008)

Microcracks in nuclear graphite and highly oriented pyrolytic graphite (HOPG)
af: Wen, K, et al.
Udgivet: (2008)

Analysis of crack propagation in nuclear graphite using three-point bending of sandwiched specimens
af: Shi, L, et al.
Udgivet: (2008)

Microstructural scale strain localisation in nuclear graphite
af: Joyce, MR, et al.
Udgivet: (2008)

Observations of strain localisation and failure in nuclear graphite
af: Joyce, MR, et al.
Udgivet: (2007)

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
af: Babout, L, et al.
Udgivet: (2006)

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
af: Babout, L, et al.
Udgivet: (2006)

Observation and quantification of three-dimensional crack propagation in poly-granular graphite
af: Mostafavi, M, et al.
Udgivet: (2013)

Observation and quantification of three-dimensional crack propagation in poly-granular graphite
af: Mostafavi, M, et al.
Udgivet: (2013)

Observation and quantification of three-dimensional crack propagation in poly-granular graphite
af: Marrow, T, et al.
Udgivet: (2012)

Annealing of ion irradiation damage in nuclear graphite
af: Lasithiotakis, M, et al.
Udgivet: (2013)

Data related to the mesoscopic structure of iso-graphite for nuclear applications
af: März, B, et al.
Udgivet: (2018)

Flexural strength and defect behaviour of polygranular graphite under different states of stress
af: Mostafavi, M, et al.
Udgivet: (2013)

Flexural strength and defect behaviour of polygranular graphite under different states of stress
af: Mostafavi, M, et al.
Udgivet: (2013)

Microstructural characterisation of nuclear grade graphite
af: Jones, A, et al.
Udgivet: (2008)

3D inspection of fabrication and degradation processes from X-ray (micro) tomography images using a hole closing algorithm
af: Babout, L, et al.
Udgivet: (2010)

IN-SITU OBSERVATION OF CRACK NUCLEATION IN NUCLEAR GRAPHITE BY DIGITAL IMAGE CORRELATION
af: Li, H, et al.
Udgivet: (2009)

Adaptive 3D algorithm to detect bridging ligaments during intergranular stress corrosion cracking of stainless steel
af: Janaszewski, M, et al.
Udgivet: (2007)

3D cellular automata fracture model for porous graphite microstructures
af: Vertyagina, Y, et al.
Udgivet: (2016)

Damage, crack growth and fracture characteristics of nuclear grade graphite using the Double Torsion technique
af: Becker, T, et al.
Udgivet: (2011)