Mapping the evolution of density in 3D of thermally oxidised graphite for nuclear applications

Mapping the evolution of density in 3D of thermally oxidised graphite for nuclear applications

This paper deals with the use of X-ray tomography and subsequent kernel operations on the reconstructed images to generate 3D density maps and phase labelling of polygranular graphite subjected to thermal oxidation which, in some respects, simulates radiolytic oxidation. This shows the suitability o...

Mô tả đầy đủ

Chi tiết về thư mục
Những tác giả chính:	Babout, L, Marrow, T, Mummery, P, Withers, P
Định dạng:	Journal article
Ngôn ngữ:	English
Được phát hành:	2006

Những quyển sách tương tự

X-ray tomographic observations applied to porosity models for the thermal properties of oxidised nuclear graphite
Bằng: Babout, L, et al.
Được phát hành: (2007)

Three-dimensional characterization and thermal property modelling of thermally oxidized nuclear graphite
Bằng: Babout, L, et al.
Được phát hành: (2008)

Failure analysis of the effects of porosity in thermally oxidised nuclear graphite using finite element modelling
Bằng: Berre, C, et al.
Được phát hành: (2008)

The effect of thermal oxidation on polycrystalline graphite studied by X-ray tomography
Bằng: Babout, L, et al.
Được phát hành: (2005)

Numerical modelling of the effects of porosity changes on the mechanical properties of nuclear graphite
Bằng: Berre, C, et al.
Được phát hành: (2006)

A multi-scale three-dimensional Cellular Automata fracture model of radiolytically oxidised nuclear graphite
Bằng: Vertyagina, Y, et al.
Được phát hành: (2017)

Fracture behaviour of radiolytically oxidised reactor core graphites: a view
Bằng: Hodgkins, A, et al.
Được phát hành: (2010)

Observation of microstructure deformation and damage in nuclear graphite
Bằng: Joyce, MR, et al.
Được phát hành: (2008)

Crack propagation resistance and damage mechanisms in nuclear graphite
Bằng: Hodgkins, A, et al.
Được phát hành: (2007)

Research activities of the Nuclear Graphite Research Group - University of Manchester
Bằng: Marsden, B, et al.
Được phát hành: (2004)

Crack propagation resistance and damage mechanisms in nuclear graphite
Bằng: Hodgkins, A, et al.
Được phát hành: (2006)

X-ray tomography observation of crack propagation in nuclear graphite
Bằng: Hodgkins, A, et al.
Được phát hành: (2006)

Microstructural modelling of nuclear graphite using multi-phase models
Bằng: Berre, C, et al.
Được phát hành: (2008)

Research activities of the Nuclear Graphite Research Group at the University of Manchester, UK
Bằng: Marsden, B, et al.
Được phát hành: (2004)

A method for the 3-D quantification of bridging ligaments during crack propagation
Bằng: Babout, L, et al.
Được phát hành: (2011)

Assessment of the fracture toughness of neutron-irradiated nuclear graphite by 3D analysis of the crack displacement field
Bằng: Jin, X, et al.
Được phát hành: (2020)

Analysis of crack propagation in nuclear graphite using three-point bending of sandwiched specimens
Bằng: Shi, L, et al.
Được phát hành: (2004)

Modelling damage in nuclear graphite
Bằng: Becker, T, et al.
Được phát hành: (2013)

The microstructure of nuclear graphite binders
Bằng: Wen, K, et al.
Được phát hành: (2008)

Nanostructures of carbon in nuclear graphite
Bằng: Wen, K, et al.
Được phát hành: (2008)

Nanostructures of carbon in nuclear graphite
Bằng: Wen, K, et al.
Được phát hành: (2008)

Microcracks in nuclear graphite and highly oriented pyrolytic graphite (HOPG)
Bằng: Wen, K, et al.
Được phát hành: (2008)

Analysis of crack propagation in nuclear graphite using three-point bending of sandwiched specimens
Bằng: Shi, L, et al.
Được phát hành: (2008)

Microstructural scale strain localisation in nuclear graphite
Bằng: Joyce, MR, et al.
Được phát hành: (2008)

Observations of strain localisation and failure in nuclear graphite
Bằng: Joyce, MR, et al.
Được phát hành: (2007)

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
Bằng: Babout, L, et al.
Được phát hành: (2006)

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
Bằng: Babout, L, et al.
Được phát hành: (2006)

Observation and quantification of three-dimensional crack propagation in poly-granular graphite
Bằng: Mostafavi, M, et al.
Được phát hành: (2013)

Observation and quantification of three-dimensional crack propagation in poly-granular graphite
Bằng: Mostafavi, M, et al.
Được phát hành: (2013)

Observation and quantification of three-dimensional crack propagation in poly-granular graphite
Bằng: Marrow, T, et al.
Được phát hành: (2012)

Annealing of ion irradiation damage in nuclear graphite
Bằng: Lasithiotakis, M, et al.
Được phát hành: (2013)

Data related to the mesoscopic structure of iso-graphite for nuclear applications
Bằng: März, B, et al.
Được phát hành: (2018)

Flexural strength and defect behaviour of polygranular graphite under different states of stress
Bằng: Mostafavi, M, et al.
Được phát hành: (2013)

Flexural strength and defect behaviour of polygranular graphite under different states of stress
Bằng: Mostafavi, M, et al.
Được phát hành: (2013)

Microstructural characterisation of nuclear grade graphite
Bằng: Jones, A, et al.
Được phát hành: (2008)

3D inspection of fabrication and degradation processes from X-ray (micro) tomography images using a hole closing algorithm
Bằng: Babout, L, et al.
Được phát hành: (2010)

IN-SITU OBSERVATION OF CRACK NUCLEATION IN NUCLEAR GRAPHITE BY DIGITAL IMAGE CORRELATION
Bằng: Li, H, et al.
Được phát hành: (2009)

Adaptive 3D algorithm to detect bridging ligaments during intergranular stress corrosion cracking of stainless steel
Bằng: Janaszewski, M, et al.
Được phát hành: (2007)

3D cellular automata fracture model for porous graphite microstructures
Bằng: Vertyagina, Y, et al.
Được phát hành: (2016)

Damage, crack growth and fracture characteristics of nuclear grade graphite using the Double Torsion technique
Bằng: Becker, T, et al.
Được phát hành: (2011)