Correlations of electrochemical noise, acoustic emission and complementary monitoring techniques during intergranular stress-corrosion cracking of austenitic stainless steel

Correlations of electrochemical noise, acoustic emission and complementary monitoring techniques during intergranular stress-corrosion cracking of austenitic stainless steel

Specimens of sensitized type AISI 304 stainless steel were subjected to constant load and exposed to an aqueous sodium thiosulphate solution. Intergranular stress-corrosion cracking was monitored simultaneously for electrochemical noise, acoustic emission, and specimen elongation. A section of the g...

Fuld beskrivelse

Bibliografiske detaljer
Main Authors:	Kovac, J, Alaux, C, Marrow, T, Govekar, E, Legat, A
Format:	Journal article
Sprog:	English
Udgivet:	2010

Lignende værker

Detection and characterisation of intergranular stress-corrosion cracking on austenitic stainless steel
af: Kovac, J, et al.
Udgivet: (2012)

A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
af: Rahimi, S, et al.
Udgivet: (2019)

A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
af: S. Rahimi, et al.
Udgivet: (2020-02-01)

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
af: Babout, L, et al.
Udgivet: (2006)

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
af: Babout, L, et al.
Udgivet: (2006)

Three dimensional observations and modelling of intergranular stress corrosion cracking in austenitic stainless steel
af: Marrow, T, et al.
Udgivet: (2006)

Influence of microstructure and stress on short intergranular stress corrosion crack growth in austenitic stainless steel type 304
af: Rahimi, S, et al.
Udgivet: (2008)

Effect of surface machining on intergranular stress corrosion cracking (IGSCC) in sensitised type 304 austenitic stainless steel
af: Rahimi, S, et al.
Udgivet: (2016)

Intergranular stress corrosion crack propagation in sensitised austenitic stainless steel (microstructure modelling and experimental observation)
af: Marrow, T, et al.
Udgivet: (2006)

Mechanical criterion for nucleation of intergranular stress corrosion cracking in austenitic stainless steel
af: Tomoyuki Fujii, et al.
Udgivet: (2021-09-01)

Effects of orientation, stress and exposure time on short intergranular stress corrosion crack behaviour in sensitised type 304 austenitic stainless steel
af: Rahimi, S, et al.
Udgivet: (2012)

Effects of orientation, stress and exposure time on short intergranular stress corrosion crack behaviour in sensitised type 304 austenitic stainless steel
af: Rahimi, S, et al.
Udgivet: (2012)

In situ observation of intergranular crack nucleation in a grain boundary controlled austenitic stainless steel.
af: Rahimi, S, et al.
Udgivet: (2009)

In situ observation of intergranular crack nucleation in a grain boundary controlled austenitic stainless steel.
af: Rahimi, S, et al.
Udgivet: (2009)

Electrochemical Analysis on Intergranular Corrosion of Austenitic Stainless Steel Weld in Molten Nitrate Salt
af: Noparat Kanjanaprayut, et al.
Udgivet: (2024-11-01)

Intergranular Corrosion Analysis of Austenitic Stainless Steels in Molten Nitrate Salt Using Electrochemical Characterization
af: Noparat Kanjanaprayut, et al.
Udgivet: (2024-01-01)

Grain boundary structure and intergranular stress corrosion crack initiation in high temperature water of a thermally sensitised austenitic stainless steel, observed in situ
af: Stratulat, A, et al.
Udgivet: (2014)

Grain boundary structure and intergranular stress corrosion crack initiation in high temperature water of a thermally sensitised austenitic stainless steel, observed in situ
af: Stratulat, A, et al.
Udgivet: (2014)

IN-SITU OBSERVATIONS OF INTERGRANULAR STRESS CORROSION CRACKING
af: Duff, J, et al.
Udgivet: (2009)

Influence of milling on the development of stress corrosion cracks in austenitic stainless steel
af: Lyon, K, et al.
Udgivet: (2014)

Nonlinear Ultrasonic Characterization for Intergranular Corrosion Susceptibility of 304 Austenitic Stainless Steel
af: HOU Tian-yu, et al.
Udgivet: (2017-10-01)

The roles of microstructure and mechanics in intergranular stress corrosion cracking
af: Jivkov, A, et al.
Udgivet: (2005)

Effect of strain path and annealing on development of resistance to intergranular degradation in austenitic stainless steels
af: Randle, V, et al.
Udgivet: (2008)

Adaptive 3D algorithm to detect bridging ligaments during intergranular stress corrosion cracking of stainless steel
af: Janaszewski, M, et al.
Udgivet: (2007)

Application of electrochemical methods for the investigation of intergranular corrosion welded joint austenitic stainless steel 19Cr-9Ni
af: Jegdić Bore V., et al.
Udgivet: (2011-01-01)

Microstructures and intergranular corrosion resistances of hot-rolled austenitic stainless steel clad plates
af: Ju-Chan Jin, et al.
Udgivet: (2023-09-01)

3D modelling of intergranular stress corrosion cracking (IGSCC)
af: Zhang, Y, et al.
Udgivet: (2009)

3D modelling of intergranular stress corrosion cracking (IGSCC)
af: Zhang, Y, et al.
Udgivet: (2009)

New techniques for intergranular stress corrosion crack observation
af: Marrow, T, et al.
Udgivet: (2008)

TEM investigations of intergranular stress corrosion cracking in austenitic alloys in PWR environmental conditions
af: Lozano-Perez, S, et al.
Udgivet: (2003)

TEM investigations of intergranular stress corrosion cracking in austenitic alloys in PWR environmental conditions
af: Lozano-Perez, S, et al.
Udgivet: (2003)

Modelling intergranular stress corrosion cracking in simulated three-dimensional microstructures
af: Jivkov, A, et al.
Udgivet: (2007)

Overview of Intergranular Fracture of Neutron Irradiated Austenitic Stainless Steels
af: Anna Hojná
Udgivet: (2017-09-01)

A two-dimensional mesoscale model for intergranular stress corrosion crack propagation
af: Jivkov, A, et al.
Udgivet: (2006)

Mesoscale mechanical model for intergranular stress corrosion cracking and implications for microstructure engineering
af: Jivkov, A, et al.
Udgivet: (2008)

Mesoscale mechanical model for intergranular stress corrosion cracking and implications for microstructure engineering
af: Jivkov, A, et al.
Udgivet: (2008)

Intergranular crack nucleation in polycrystalline alumina
af: Aswad, M, et al.
Udgivet: (2010)

Intergranular crack nuclei in polycrystalline alumina
af: Aswad, M, et al.
Udgivet: (2012)

Intergranular crack nucleation in polycrystalline alumina
af: Aswad, M, et al.
Udgivet: (2010)

Intergranular crack nuclei in polycrystalline alumina
af: Aswad, M, et al.
Udgivet: (2012)