A phase field formulation for hydrogen assisted cracking

A phase field formulation for hydrogen assisted cracking

We present a phase field modeling framework for hydrogen assisted cracking. The model builds upon a coupled mechanical and hydrogen diffusion response, driven by chemical potential gradients, and a hydrogen-dependent fracture energy degradation law grounded on first principles calculations. The coup...

Disgrifiad llawn

Manylion Llyfryddiaeth
Prif Awduron:	Martinez-Paneda, E, Golahmar, A, Niordson, CF
Fformat:	Journal article
Iaith:	English
Cyhoeddwyd:	Elsevier 2018

Eitemau Tebyg

A phase field model for hydrogen-assisted fatigue
gan: Golahmar, A, et al.
Cyhoeddwyd: (2021)

Applications of phase field fracture in modelling hydrogen assisted failures
gan: Kristensen, PK, et al.
Cyhoeddwyd: (2020)

A phase field model for high-cycle fatigue: total-life analysis
gan: Golahmar, A, et al.
Cyhoeddwyd: (2023)

Strain gradient plasticity-based modeling of hydrogen environment assisted cracking
gan: Martinez-Paneda, E, et al.
Cyhoeddwyd: (2016)

Accelerated high-cycle phase field fatigue predictions
gan: Kristensen, PK, et al.
Cyhoeddwyd: (2023)

An assessment of phase field fracture: crack initiation and growth
gan: Kristensen, PK, et al.
Cyhoeddwyd: (2021)

A phase field model for elastic-gradient-plastic solids undergoing hydrogen embrittlement
gan: Kristensen, PK, et al.
Cyhoeddwyd: (2020)

Strain gradient plasticity modeling of hydrogen diffusion to the crack tip
gan: Martinez-Paneda, E, et al.
Cyhoeddwyd: (2016)

A phase field formulation for dissolution-driven stress corrosion cracking
gan: Cui, C, et al.
Cyhoeddwyd: (2020)

A mechanism-based multi-trap phase field model for hydrogen assisted fracture
gan: Isfandbod, M, et al.
Cyhoeddwyd: (2021)

A coupled phase field formulation for modelling fatigue cracking in lithium-ion battery electrode particles
gan: Ai, W, et al.
Cyhoeddwyd: (2022)

Computational predictions of hydrogen-assisted fatigue crack growth
gan: Cui, C, et al.
Cyhoeddwyd: (2024)

The role of plastic strain gradients in the crack growth resistance of metals
gan: Martínez-Pañeda, E, et al.
Cyhoeddwyd: (2019)

A generalised, multi-phase-field theory for dissolution-driven stress corrosion cracking and hydrogen embrittlement
gan: Cui, C, et al.
Cyhoeddwyd: (2022)

Cohesive zone modelling of hydrogen assisted fatigue crack growth: the role of trapping
gan: Fernández-Sousa, R, et al.
Cyhoeddwyd: (2022)

Progress and opportunities in modelling environmentally assisted cracking
gan: Martinez-Paneda, E
Cyhoeddwyd: (2021)

On fracture in finite strain gradient plasticity
gan: Martínez-Pañeda, E, et al.
Cyhoeddwyd: (2015)

Phase field modelling of crack propagation in functionally graded materials
gan: Hirshikesh, et al.
Cyhoeddwyd: (2019)

Adaptive phase field modelling of crack propagation in orthotropic functionally graded materials
gan: Martinez-Paneda, E, et al.
Cyhoeddwyd: (2020)

On the suitability of single-edge notch tension (SENT) testing for assessing hydrogen-assisted cracking susceptibility
gan: Cupertino-Malheiros, L, et al.
Cyhoeddwyd: (2024)

Phase field cohesive zone modeling for fatigue crack propagation in quasi-brittle materials
gan: Baktheer, A, et al.
Cyhoeddwyd: (2024)

A phase field-based framework for electro-chemo-mechanical fracture: crack-contained electrolytes, chemical reactions and stabilisation
gan: Hageman, T, et al.
Cyhoeddwyd: (2023)

A finite element framework for distortion gradient plasticity with applications to bending of thin foils
gan: Martínez-Pañeda, E, et al.
Cyhoeddwyd: (2016)

A phase-field chemo-mechanical model for corrosion-induced cracking in reinforced concrete
gan: Korec, E, et al.
Cyhoeddwyd: (2023)

Hydrogen-assisted fatigue crack growth: pre-charging vs in-situ testing in gaseous environments
gan: Zafra, A, et al.
Cyhoeddwyd: (2023)

Generalised boundary conditions for hydrogen transport at crack tips
gan: Martínez-Pañeda, E, et al.
Cyhoeddwyd: (2020)

A microstructure-sensitive electro-chemo-mechanical phase-field model of pitting and stress corrosion cracking
gan: Makuch, M, et al.
Cyhoeddwyd: (2024)

A generalised phase field model for fatigue crack growth in elastic–plastic solids with an efficient monolithic solver
gan: Khalil, Z, et al.
Cyhoeddwyd: (2021)

An FFT-based crystal plasticity phase-field model for micromechanical fatigue cracking based on the stored energy density
gan: Lucarini, S, et al.
Cyhoeddwyd: (2023)

Phase-field modeling of pitting and mechanically-assisted corrosion of Mg alloys for biomedical applications
gan: Kovacevic, S, et al.
Cyhoeddwyd: (2023)

A micro-mechanics based extension of the GTN continuum model accounting for random void distributions
gan: Holte, I, et al.
Cyhoeddwyd: (2023)

Analysis of the influence of microstructural traps on hydrogen assisted fatigue
gan: Fernández-Sousa, R, et al.
Cyhoeddwyd: (2020)

A phase field electro-chemo-mechanical formulation for predicting void evolution at the Li–electrolyte interface in all-solid-state batteries
gan: Zhao, Y, et al.
Cyhoeddwyd: (2022)

Steady-state fracture toughness of elastic-plastic solids: isotropic versus kinematic hardening
gan: Juul, KJ, et al.
Cyhoeddwyd: (2019)

Phase-field chemo-mechanical modelling of corrosion-induced cracking in reinforced concrete subjected to non-uniform chloride-induced corrosion
gan: Korec, E, et al.
Cyhoeddwyd: (2023)

Phase-field simulations opening new horizons in corrosion research
gan: Martínez-Pañeda, E
Cyhoeddwyd: (2024)

Computational modelling of hydrogen assisted fracture in polycrystalline materials
gan: Valverde-González, A, et al.
Cyhoeddwyd: (2022)

Hydrogen assisted cracking of high strength steel welds
gan: Gedeon, Steven Anthony
Cyhoeddwyd: (2005)

Crack tip fields and fracture resistance parameters based on strain gradient plasticity
gan: Shlyannikov, V, et al.
Cyhoeddwyd: (2020)

Interaction of void spacing and material size effect on inter-void flow localization
gan: Holte, I, et al.
Cyhoeddwyd: (2020)