Radiation induced segregation and precipitation in self-ion irradiated Ferritic/Martensitic HT9 steel
<p>In this study, Ferritic/Martensitic (F/M) HT9 steel was irradiated to 20 displacements per atom (dpa) at 600 nm depth at 420 and 440˚C, and to 1, 10 and 20 dpa at 600 nm depth at 470˚C using 5 MeV Fe++ ions. The characterization was conducted using ChemiSTEM and Atom Probe Tomography (APT),...
| Príomhchruthaitheoirí: | , , , |
|---|---|
| Formáid: | Journal article |
| Foilsithe / Cruthaithe: |
Elsevier
2017
|