Processing of bulk hierarchical metal-metal composites
<p>Spray forming with co-injection of a solid particulate phase to form a metal-metal composite has been studied as a new route for manufacture. Two Al-based matrices were investigated: Al-12Si for testing the feasibility of the new manufacturing route and Al-4Cu for providing better mechanica...
| Main Author: | |
|---|---|
| Other Authors: | |
| Format: | Thesis |
| Language: | English |
| Published: |
2011
|
| Subjects: |
| _version_ | 1826304631120068608 |
|---|---|
| author | Kelly, A |
| author2 | Grant, P |
| author_facet | Grant, P Kelly, A |
| author_sort | Kelly, A |
| collection | OXFORD |
| description | <p>Spray forming with co-injection of a solid particulate phase to form a metal-metal composite has been studied as a new route for manufacture. Two Al-based matrices were investigated: Al-12Si for testing the feasibility of the new manufacturing route and Al-4Cu for providing better mechanical performance. For both composite types, Ti was chosen as the particulate phase and the processing-microstructure-property relationships then studied.</p> <p>At Peak Werkstoff GmbH, Germany 12 wt%Ti particles were co-injected into an atomised Al alloy droplet spray and co-deposited to form a &Tilde;300 kg billet. The microstructure comprised refined equiaxed α-Al grains (&Tilde;5μm), spherical Si particles (&Tilde;5μm) and uniformly distributed Ti particles (&Tilde;80μm). Sections of the billet were extruded under a range of conditions into long strips 20mm wide and 6mm, 2.5mm and 1mm thickness. At high strains, the Ti particles were deformed into continuous fibres of a few microns in thickness. Accumulative roll bonding was then performed to higher total strains, while maintaining a constant cross-section, reducing the Ti fibres to sub-micron thickness. The fibres were studied by extraction after selective dissolution of the α-Al matrix. There was no interfacial reaction between α-Al and Ti or any measurable oxide formation, thus providing encouragement for the manufacture of metal-metal composites by co-spray forming.</p> <p>A powder injection pump was successfully integrated and commissioned on the spray forming facility at Oxford University. The pump was calibrated to optimise powder flow rates. Three Al-4Cu+Ti composite billets were processed with each containing Ti powder with a different processing history. Up to 20vol%Ti was successfully incorporated, however due to the cooling effect from powder injection, porosity was significant. The quenching effect provided a finer Al-4Cu grain structure in the region of Ti injection, and also promoted precipitation of θ'-Al2Cu precipitates. A Ti/Al-4Cu interfacial reaction was more prominent in the billet spray formed at 850°C than those spray formed at 750°C.</p> <p>Angular Ti processed by a hydride-dehydride route had better deformation characteristics than spherical gas atomised Ti. Deformation processing by extrusion and rolling was investigated for Al-4Cu+20vol%Ti using SEM, EBSD and FIB. After extrusion to a strain of 5, the composite contained elongated reinforcing fibres characteristic of metal-metal composites. The microstructure studied by EBSD revealed equiaxed polygonal Al-4Cu matrix grains. Rolling was not as efficient as extrusion in producing elongated Ti fibres and was attributed to a lower deformation processing temperature. The rolled composites consisted of elongated Al-4Cu grains 1-5μm in thickness. An UTS of 339MPa at a strain of 3 was attributed to texture strengthening in the α-Al. </p> |
| first_indexed | 2024-03-07T06:20:44Z |
| format | Thesis |
| id | oxford-uuid:f2a1d2f5-dca8-450d-8eff-0ce7812445da |
| institution | University of Oxford |
| language | English |
| last_indexed | 2024-03-07T06:20:44Z |
| publishDate | 2011 |
| record_format | dspace |
| spelling | oxford-uuid:f2a1d2f5-dca8-450d-8eff-0ce7812445da2022-03-27T12:05:22ZProcessing of bulk hierarchical metal-metal compositesThesishttp://purl.org/coar/resource_type/c_db06uuid:f2a1d2f5-dca8-450d-8eff-0ce7812445daMetallurgyMaterials SciencesSpray processingEnglish2011Kelly, AGrant, PSmith, GGalano, M<p>Spray forming with co-injection of a solid particulate phase to form a metal-metal composite has been studied as a new route for manufacture. Two Al-based matrices were investigated: Al-12Si for testing the feasibility of the new manufacturing route and Al-4Cu for providing better mechanical performance. For both composite types, Ti was chosen as the particulate phase and the processing-microstructure-property relationships then studied.</p> <p>At Peak Werkstoff GmbH, Germany 12 wt%Ti particles were co-injected into an atomised Al alloy droplet spray and co-deposited to form a &Tilde;300 kg billet. The microstructure comprised refined equiaxed α-Al grains (&Tilde;5μm), spherical Si particles (&Tilde;5μm) and uniformly distributed Ti particles (&Tilde;80μm). Sections of the billet were extruded under a range of conditions into long strips 20mm wide and 6mm, 2.5mm and 1mm thickness. At high strains, the Ti particles were deformed into continuous fibres of a few microns in thickness. Accumulative roll bonding was then performed to higher total strains, while maintaining a constant cross-section, reducing the Ti fibres to sub-micron thickness. The fibres were studied by extraction after selective dissolution of the α-Al matrix. There was no interfacial reaction between α-Al and Ti or any measurable oxide formation, thus providing encouragement for the manufacture of metal-metal composites by co-spray forming.</p> <p>A powder injection pump was successfully integrated and commissioned on the spray forming facility at Oxford University. The pump was calibrated to optimise powder flow rates. Three Al-4Cu+Ti composite billets were processed with each containing Ti powder with a different processing history. Up to 20vol%Ti was successfully incorporated, however due to the cooling effect from powder injection, porosity was significant. The quenching effect provided a finer Al-4Cu grain structure in the region of Ti injection, and also promoted precipitation of θ'-Al2Cu precipitates. A Ti/Al-4Cu interfacial reaction was more prominent in the billet spray formed at 850°C than those spray formed at 750°C.</p> <p>Angular Ti processed by a hydride-dehydride route had better deformation characteristics than spherical gas atomised Ti. Deformation processing by extrusion and rolling was investigated for Al-4Cu+20vol%Ti using SEM, EBSD and FIB. After extrusion to a strain of 5, the composite contained elongated reinforcing fibres characteristic of metal-metal composites. The microstructure studied by EBSD revealed equiaxed polygonal Al-4Cu matrix grains. Rolling was not as efficient as extrusion in producing elongated Ti fibres and was attributed to a lower deformation processing temperature. The rolled composites consisted of elongated Al-4Cu grains 1-5μm in thickness. An UTS of 339MPa at a strain of 3 was attributed to texture strengthening in the α-Al. </p> |
| spellingShingle | Metallurgy Materials Sciences Spray processing Kelly, A Processing of bulk hierarchical metal-metal composites |
| title | Processing of bulk hierarchical metal-metal composites |
| title_full | Processing of bulk hierarchical metal-metal composites |
| title_fullStr | Processing of bulk hierarchical metal-metal composites |
| title_full_unstemmed | Processing of bulk hierarchical metal-metal composites |
| title_short | Processing of bulk hierarchical metal-metal composites |
| title_sort | processing of bulk hierarchical metal metal composites |
| topic | Metallurgy Materials Sciences Spray processing |
| work_keys_str_mv | AT kellya processingofbulkhierarchicalmetalmetalcomposites |