A phase-field chemo-mechanical model for corrosion-induced cracking in reinforced concrete

A phase-field chemo-mechanical model for corrosion-induced cracking in reinforced concrete

We present a new mechanistic framework for corrosion-induced cracking in reinforced concrete that resolves the underlying chemo-mechanical processes. The framework combines, for the first time, (i) a model for reactive transport and precipitation of dissolved Fe<sup>2+</sup> and Fe<su...

Mô tả đầy đủ

Chi tiết về thư mục
Những tác giả chính:	Korec, E, Jirásek, M, Wong, HS, Martínez-Pañeda, E
Định dạng:	Journal article
Ngôn ngữ:	English
Được phát hành:	Elsevier 2023

Những quyển sách tương tự

Phase-field chemo-mechanical modelling of corrosion-induced cracking in reinforced concrete subjected to non-uniform chloride-induced corrosion
Bằng: Korec, E, et al.
Được phát hành: (2023)

A microstructure-sensitive electro-chemo-mechanical phase-field model of pitting and stress corrosion cracking
Bằng: Makuch, M, et al.
Được phát hành: (2024)

Predicting the impact of water transport on carbonation-induced corrosion in variably saturated reinforced concrete
Bằng: Korec, E, et al.
Được phát hành: (2024)

Electro-chemo-mechanical phase field modeling of localized corrosion: theory and COMSOL implementation
Bằng: Cui, C, et al.
Được phát hành: (2023)

A phase field-based framework for electro-chemo-mechanical fracture: crack-contained electrolytes, chemical reactions and stabilisation
Bằng: Hageman, T, et al.
Được phát hành: (2023)

A phase field formulation for dissolution-driven stress corrosion cracking
Bằng: Cui, C, et al.
Được phát hành: (2020)

A generalised, multi-phase-field theory for dissolution-driven stress corrosion cracking and hydrogen embrittlement
Bằng: Cui, C, et al.
Được phát hành: (2022)

Phase-field simulations opening new horizons in corrosion research
Bằng: Martínez-Pañeda, E
Được phát hành: (2024)

A phase field electro-chemo-mechanical formulation for predicting void evolution at the Li–electrolyte interface in all-solid-state batteries
Bằng: Zhao, Y, et al.
Được phát hành: (2022)

Steel rebar corrosion and corrosion-induced cracking in reinforced foamed concrete
Bằng: Yongheng Luo, et al.
Được phát hành: (2022-10-01)

An assessment of phase field fracture: crack initiation and growth
Bằng: Kristensen, PK, et al.
Được phát hành: (2021)

A phase field formulation for hydrogen assisted cracking
Bằng: Martinez-Paneda, E, et al.
Được phát hành: (2018)

Phase-field modeling of pitting and mechanically-assisted corrosion of Mg alloys for biomedical applications
Bằng: Kovacevic, S, et al.
Được phát hành: (2023)

Phase field modelling of crack propagation in functionally graded materials
Bằng: Hirshikesh, et al.
Được phát hành: (2019)

Microcell and macrocell corrosion of steel bars and corrosion-induced concrete cracking in reinforced concrete slabs
Bằng: Bui, Huy Tang
Được phát hành: (2023)

Adaptive phase field modelling of crack propagation in orthotropic functionally graded materials
Bằng: Martinez-Paneda, E, et al.
Được phát hành: (2020)

Repair of cracked reinforced concrete : assesment of corrosion protection/
Bằng: 209164 Calder, A. J. J., et al.
Được phát hành: (1988)

An electro-chemo-mechanical framework for predicting hydrogen uptake in metals due to aqueous electrolytes
Bằng: Hageman, T, et al.
Được phát hành: (2022)

Application of phase-field method in corrosion fracture of reinforced concrete
Bằng: Caihong Zhang, et al.
Được phát hành: (2022-06-01)

The role of chemo-mechanical modelling in the development of battery technology – a perspective
Bằng: Boyce, AM, et al.
Được phát hành: (2024)

Phase field cohesive zone modeling for fatigue crack propagation in quasi-brittle materials
Bằng: Baktheer, A, et al.
Được phát hành: (2024)

Relationship between Corrosion of Reinforcement and Surface Cracking Width in Concrete
Bằng: Jian Cao, et al.
Được phát hành: (2020-01-01)

Adaptive phase field modelling of crack propagation in orthotropic functionally graded materials
Bằng: Hirshikesh, et al.
Được phát hành: (2021-02-01)

Phase field predictions of microscopic fracture and R-curve behaviour of fibre-reinforced composites
Bằng: Tan, W, et al.
Được phát hành: (2020)

Detection of corrosion-induced cracks in reinforced concrete using Rayleigh wave method
Bằng: Chua, Isabelle Mui Koon
Được phát hành: (2023)

An FFT-based crystal plasticity phase-field model for micromechanical fatigue cracking based on the stored energy density
Bằng: Lucarini, S, et al.
Được phát hành: (2023)

A coupled phase field formulation for modelling fatigue cracking in lithium-ion battery electrode particles
Bằng: Ai, W, et al.
Được phát hành: (2022)

Investigation of Corrosion Product Distribution and Induced Cracking Patterns in Reinforced Concrete Using Accelerated Corrosion Testing
Bằng: Olfa Loukil, et al.
Được phát hành: (2024-12-01)

Correlation between surface crack width and steel corrosion in reinforced concrete
Bằng: Mak Michele Win Tai, et al.
Được phát hành: (2018-01-01)

Simulation and analysis of corrosion fracture of reinforced concrete based on phase field method
Bằng: Wenqiang Xu, et al.
Được phát hành: (2022-12-01)

Comparative Analysis of Concrete Cracking and Reinforcement Corrosion in Concrete and Ultra-High-Performance Concrete Short Columns after Accelerated Corrosion
Bằng: Hengyu Wu, et al.
Được phát hành: (2024-09-01)

A generalised phase field model for fatigue crack growth in elastic–plastic solids with an efficient monolithic solver
Bằng: Khalil, Z, et al.
Được phát hành: (2021)

Multi-peak nonuniform model of rust distribution and corrosion-induced concrete cracking in reinforced concrete slabs
Bằng: Bui, Huy Tang, et al.
Được phát hành: (2023)

Predicting the Width of Corrosion-Induced Cracks in Reinforced Concrete Using a Damage Model Based on Fracture Mechanics
Bằng: Shinichiro Okazaki, et al.
Được phát hành: (2020-07-01)

Degradation Monitoring in Reinforced Concrete with 3D Localization of Rebar Corrosion and Related Concrete Cracking
Bằng: Charlotte Van Steen, et al.
Được phát hành: (2021-07-01)

Prediction of corroded reinforced concrete slab during chloride-induced corrosion process using corrosion-induced crack widths
Bằng: Kim, Jing Zhe
Được phát hành: (2023)

4D evolutions of cracks, voids, and corrosion products in reinforced concrete materials
Bằng: Jaber Taheri-Shakib, et al.
Được phát hành: (2023-12-01)

CRACK GROWTH RESISTANCE INCREASE OF REINFORCED CONCRETE DAMAGED BY CORROSION WITH REDUCTION OF PRESTRESSING
Bằng: O V Baydin
Được phát hành: (2012-09-01)

EFFECT OF PRESTRESSED FORCE AND SIZE OF REINFORCEMENT ON CORROSION CRACK WIDTH IN CONCRETE MEMBER
Bằng: AGUS MARYOTO, et al.
Được phát hành: (2017-10-01)

The role of chemo-mechanical modelling in the development of battery technology—a perspective
Bằng: Adam M Boyce, et al.
Được phát hành: (2024-01-01)