Notched strength of fiber-reinforced polymer (FRP) / Norhazwan Norizan
This project involved in the study of notched strength reduction and determination of damage zone, aₒ, of E-glass, Kevlar and Carbon Fiber/Epoxy composite laminates. The specimen configuration used for this project was 101.6 mmx 101.6 mm with 30 mm diameter central hole and was subjected to bi-axial...
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English |
| Published: |
2005
|
| Subjects: | |
| Online Access: | https://ir.uitm.edu.my/id/eprint/21302/1/TD_NORHAZWAN%20NORIZAN%20EM%2005_5.pdf |
| _version_ | 1796901341433430016 |
|---|---|
| author | Norizan, Norhazwan |
| author_facet | Norizan, Norhazwan |
| author_sort | Norizan, Norhazwan |
| collection | UITM |
| description | This project involved in the study of notched strength reduction and determination of damage zone, aₒ, of E-glass, Kevlar and Carbon Fiber/Epoxy composite laminates. The specimen configuration used for this project was 101.6 mmx 101.6 mm with 30 mm diameter central hole and was subjected to bi-axial loading condition using a special grip and fixture. The damage zones, aₒ, was determined experimentally using optical microscope. Using the values aₒ, the notched strength of the laminates were then determined using both Average Stress Criterion (ASC) and the Fracture Mechanics Criterion (FMC). These calculated values of notched strengths were then compared with that determined through experimentation. In this project, the results indicated that the notched strengths of the glass fiber/epoxy using the Average Stress Criterion and Fracture Mechanics Criterion are comparable. However, the notched strength predicted by the Fracture Mechanics Criterion was about 50% indifference with the Average Stress Criterion for Kevlar and carbon fiber/epoxy. This might be due to the determination of fracture toughness, Kc, using isotropic solution may not be suitable for these materials. Experimental values of the notched strengths of the laminates under bi-axial loading in the experiments cannot be acceptable due to the problems occurred at the grip. Further improvements are needed to overcome the grip problems or new fixture should be designed and constructed in order to obtain better results in the future. |
| first_indexed | 2024-03-06T01:48:38Z |
| format | Thesis |
| id | uitm.eprints-1302 |
| institution | Universiti Teknologi MARA |
| language | English |
| last_indexed | 2024-03-06T01:48:38Z |
| publishDate | 2005 |
| record_format | dspace |
| spelling | uitm.eprints-13022018-10-02T07:42:58Z https://ir.uitm.edu.my/id/eprint/21302/ Notched strength of fiber-reinforced polymer (FRP) / Norhazwan Norizan Norizan, Norhazwan Polymers and polymer manufacture This project involved in the study of notched strength reduction and determination of damage zone, aₒ, of E-glass, Kevlar and Carbon Fiber/Epoxy composite laminates. The specimen configuration used for this project was 101.6 mmx 101.6 mm with 30 mm diameter central hole and was subjected to bi-axial loading condition using a special grip and fixture. The damage zones, aₒ, was determined experimentally using optical microscope. Using the values aₒ, the notched strength of the laminates were then determined using both Average Stress Criterion (ASC) and the Fracture Mechanics Criterion (FMC). These calculated values of notched strengths were then compared with that determined through experimentation. In this project, the results indicated that the notched strengths of the glass fiber/epoxy using the Average Stress Criterion and Fracture Mechanics Criterion are comparable. However, the notched strength predicted by the Fracture Mechanics Criterion was about 50% indifference with the Average Stress Criterion for Kevlar and carbon fiber/epoxy. This might be due to the determination of fracture toughness, Kc, using isotropic solution may not be suitable for these materials. Experimental values of the notched strengths of the laminates under bi-axial loading in the experiments cannot be acceptable due to the problems occurred at the grip. Further improvements are needed to overcome the grip problems or new fixture should be designed and constructed in order to obtain better results in the future. 2005 Thesis NonPeerReviewed text en https://ir.uitm.edu.my/id/eprint/21302/1/TD_NORHAZWAN%20NORIZAN%20EM%2005_5.pdf Notched strength of fiber-reinforced polymer (FRP) / Norhazwan Norizan. (2005) Degree thesis, thesis, Universiti Teknologi MARA. <http://terminalib.uitm.edu.my/21302.pdf> |
| spellingShingle | Polymers and polymer manufacture Norizan, Norhazwan Notched strength of fiber-reinforced polymer (FRP) / Norhazwan Norizan |
| title | Notched strength of fiber-reinforced polymer (FRP) / Norhazwan Norizan |
| title_full | Notched strength of fiber-reinforced polymer (FRP) / Norhazwan Norizan |
| title_fullStr | Notched strength of fiber-reinforced polymer (FRP) / Norhazwan Norizan |
| title_full_unstemmed | Notched strength of fiber-reinforced polymer (FRP) / Norhazwan Norizan |
| title_short | Notched strength of fiber-reinforced polymer (FRP) / Norhazwan Norizan |
| title_sort | notched strength of fiber reinforced polymer frp norhazwan norizan |
| topic | Polymers and polymer manufacture |
| url | https://ir.uitm.edu.my/id/eprint/21302/1/TD_NORHAZWAN%20NORIZAN%20EM%2005_5.pdf |
| work_keys_str_mv | AT norizannorhazwan notchedstrengthoffiberreinforcedpolymerfrpnorhazwannorizan |