Effect of silica doped zinc oxide based varistor on structural and electrical properties / Nordiana Osman
Zinc Oxide (ZnO) based varistor are widely used as circuit protective devices by literally absorbs the dangerous surge and spikes or grounding this unwanted magnitude. In this research, the effect of silica (SiO2) doping on the microstructure and electrical properties of ZnO base varistor has bee...
| Main Author: | |
|---|---|
| Format: | Student Project |
| Language: | English |
| Published: |
Faculty of Applied Sciences
2017
|
| Subjects: | |
| Online Access: | https://ir.uitm.edu.my/id/eprint/23776/1/PPb_NORDIANA%20OSMAN%20AS%20C%2017_5.PDF |
| _version_ | 1796901797867028480 |
|---|---|
| author | Osman, Nordiana |
| author_facet | Osman, Nordiana |
| author_sort | Osman, Nordiana |
| collection | UITM |
| description | Zinc Oxide (ZnO) based varistor are widely used as circuit protective devices by
literally absorbs the dangerous surge and spikes or grounding this unwanted
magnitude. In this research, the effect of silica (SiO2) doping on the microstructure
and electrical properties of ZnO base varistor has been investigated. The sample
undoped ZnO and 1 wt.%, 3 wt.%, 5 wt.% and 7 wt.% SiO2 doped ZnO were
prepared by using solid state method. The sample have been characterized via X-Ray
Diffraction (XRD), Scanning Electron Microscopy (SEM), densification and
electrical measurement. All the XRD diffraction peak was shows the presence of
dominant ZnO phase with hexagonal wurtzite structure. The SEM results show that
the average grain size of undoped ZnO was low compared to SiO2 doped ZnO. The
average grain size increased with the increases of SiO2 dopant and the structural of 5
wt.% of SiO2 was more homogeneous and uniformly distributed. The value of
nonlinear coefficient (a) was obtained from the analysis of I-V curve. The a value of
undoped ZnO sample is low compared to SiO2 doped ZnO. The a value is increased
as the content of Si02increases. The maximum value of α is at 5 wt.% of SiO2 doped
ZnO which is 2.040 and might be enhanced the performance of varistor. |
| first_indexed | 2024-03-06T01:55:25Z |
| format | Student Project |
| id | uitm.eprints-3776 |
| institution | Universiti Teknologi MARA |
| language | English |
| last_indexed | 2024-03-06T01:55:25Z |
| publishDate | 2017 |
| publisher | Faculty of Applied Sciences |
| record_format | dspace |
| spelling | uitm.eprints-37762019-04-09T01:47:20Z https://ir.uitm.edu.my/id/eprint/23776/ Effect of silica doped zinc oxide based varistor on structural and electrical properties / Nordiana Osman Osman, Nordiana Inorganic chemistry Zinc Oxide (ZnO) based varistor are widely used as circuit protective devices by literally absorbs the dangerous surge and spikes or grounding this unwanted magnitude. In this research, the effect of silica (SiO2) doping on the microstructure and electrical properties of ZnO base varistor has been investigated. The sample undoped ZnO and 1 wt.%, 3 wt.%, 5 wt.% and 7 wt.% SiO2 doped ZnO were prepared by using solid state method. The sample have been characterized via X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), densification and electrical measurement. All the XRD diffraction peak was shows the presence of dominant ZnO phase with hexagonal wurtzite structure. The SEM results show that the average grain size of undoped ZnO was low compared to SiO2 doped ZnO. The average grain size increased with the increases of SiO2 dopant and the structural of 5 wt.% of SiO2 was more homogeneous and uniformly distributed. The value of nonlinear coefficient (a) was obtained from the analysis of I-V curve. The a value of undoped ZnO sample is low compared to SiO2 doped ZnO. The a value is increased as the content of Si02increases. The maximum value of α is at 5 wt.% of SiO2 doped ZnO which is 2.040 and might be enhanced the performance of varistor. Faculty of Applied Sciences 2017 Student Project NonPeerReviewed text en https://ir.uitm.edu.my/id/eprint/23776/1/PPb_NORDIANA%20OSMAN%20AS%20C%2017_5.PDF Effect of silica doped zinc oxide based varistor on structural and electrical properties / Nordiana Osman. (2017) [Student Project] <http://terminalib.uitm.edu.my/23776.pdf> (Unpublished) |
| spellingShingle | Inorganic chemistry Osman, Nordiana Effect of silica doped zinc oxide based varistor on structural and electrical properties / Nordiana Osman |
| title | Effect of silica doped zinc oxide based varistor on
structural and electrical properties / Nordiana Osman |
| title_full | Effect of silica doped zinc oxide based varistor on
structural and electrical properties / Nordiana Osman |
| title_fullStr | Effect of silica doped zinc oxide based varistor on
structural and electrical properties / Nordiana Osman |
| title_full_unstemmed | Effect of silica doped zinc oxide based varistor on
structural and electrical properties / Nordiana Osman |
| title_short | Effect of silica doped zinc oxide based varistor on
structural and electrical properties / Nordiana Osman |
| title_sort | effect of silica doped zinc oxide based varistor on structural and electrical properties nordiana osman |
| topic | Inorganic chemistry |
| url | https://ir.uitm.edu.my/id/eprint/23776/1/PPb_NORDIANA%20OSMAN%20AS%20C%2017_5.PDF |
| work_keys_str_mv | AT osmannordiana effectofsilicadopedzincoxidebasedvaristoronstructuralandelectricalpropertiesnordianaosman |