Nitridation of AL-Mg-Si alloys through dynamic heating = Penitridaan aloi AL-Mg-Si secara pemanasan dinamik
Nitridation behaviour of Al-Mg-Si alloys was studied as a function of temperature by means of thermogravimetry method. A reactive gas, N2-4%H2 at a rate of 10 ml/min was purged into the thermogravimetry analyser chamber. The Al alloys were heated from 25oC to 625oC at the heating rate of 15oC/min...
Main Authors: | Roslinda Shamsudin, Saiful Rizam Shamsuddin, Abdul Razak Daud, Muhammad Azmi Abdul Hamid |
---|---|
Format: | Article |
Language: | English |
Published: |
Universiti Kebangsaan Malaysia
2007
|
Online Access: | http://journalarticle.ukm.my/105/1/1.pdf |
Similar Items
-
Effects of magnesium addition on microhardness in eutectic Al-Si-Mg Alloys
by: Abdul Razak Daud,, et al.
Published: (2001) -
Effect of barium on the structure and characteristics of Mg2Si reinforced particles Al–Mg2Si–Cu in situ composite
by: Nordin, Nur Azmah, et al.
Published: (2020) -
Al-Si and Al-Si-Mg Cast Alloys Shrinkage Porosity Estimation
by: Samavedam S., et al.
Published: (2016-03-01) -
The Influence of the Chemical Composition on the Corrosion Performances of Some Al-Fe-Si, Al-Mg-Si and Al-Mg-Mn Type of Alloys
by: Kemal Delijić, et al.
Published: (2014-12-01) -
Effect of Sever Plastic Deformation on The-Microstructure of Al-Si/Mg2Si in Situ Composites
by: Nawal Ezzat Abdul-Latiff, et al.
Published: (2016-07-01)