Characteristics of gadolinium doped cerium at different calcination temperatures for intermediate temperature SOFC
Gadolinium doped cerium (Ce0.9Gd0.1O1.95 or GDC10) was successfully synthesized using the solid-state method. Commercially available CeO2 and Gd2 O3 powders were used as starting materials. They were mixed in a ball mill where alumina balls were added as grinding medium with the ratio to powd...
| Main Authors: | , , , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Penerbit Universiti Kebangsaan Malaysia
2020
|
| Online Access: | http://journalarticle.ukm.my/16183/1/30.pdf |
| _version_ | 1796932419863969792 |
|---|---|
| author | Damisih, Hapsari, Ade Utami Agustanhakri, Deni, Yelvia Arjasa, Oka Pradipta Anggaravidya, Mahendra Raharjo, Jarot Mahendra Rao Somalu, |
| author_facet | Damisih, Hapsari, Ade Utami Agustanhakri, Deni, Yelvia Arjasa, Oka Pradipta Anggaravidya, Mahendra Raharjo, Jarot Mahendra Rao Somalu, |
| author_sort | Damisih, |
| collection | UKM |
| description | Gadolinium doped cerium (Ce0.9Gd0.1O1.95 or GDC10) was successfully synthesized using the solid-state method.
Commercially available CeO2
and Gd2
O3
powders were used as starting materials. They were mixed in a ball mill where
alumina balls were added as grinding medium with the ratio to powders as of 1:2. The obtained powders were dried and
then calcined at temperatures of 600, 700 and 800 °C, respectively. The objective of this research was to investigate the
effects of calcination temperature on the properties of GDC10. The powders were characterized using XRF, TGA, XRD,
and PSA instruments. XRF analysis shows the presence of Ce, Gd and O elements in stoichiometric composition without
any impurities. XRD analysis showed single phase structure of CeO2
where the crystallite size and lattice parameter
increases and decreases, respectively, as the calcination temperature increases. The smallest particle size of 647.3
nm was obtained at the calcination temperature of 600 °C. The density of all GDC10 samples sintered at 1350 °C was
found to be higher than 95%. In addition, the calcination temperature also influenced the ionic conductivity where
the highest obtained value was 0.0153 S.cm-1 at 800 °C for the sample calcinaed at 600 °C. The results suggest that the
calcination temperature affected the properties of GDC10 for solid oxide fuel cell application. |
| first_indexed | 2024-03-06T04:32:10Z |
| format | Article |
| id | ukm.eprints-16183 |
| institution | Universiti Kebangsaan Malaysia |
| language | English |
| last_indexed | 2024-03-06T04:32:10Z |
| publishDate | 2020 |
| publisher | Penerbit Universiti Kebangsaan Malaysia |
| record_format | dspace |
| spelling | ukm.eprints-161832021-02-13T14:28:35Z http://journalarticle.ukm.my/16183/ Characteristics of gadolinium doped cerium at different calcination temperatures for intermediate temperature SOFC Damisih, Hapsari, Ade Utami Agustanhakri, Deni, Yelvia Arjasa, Oka Pradipta Anggaravidya, Mahendra Raharjo, Jarot Mahendra Rao Somalu, Gadolinium doped cerium (Ce0.9Gd0.1O1.95 or GDC10) was successfully synthesized using the solid-state method. Commercially available CeO2 and Gd2 O3 powders were used as starting materials. They were mixed in a ball mill where alumina balls were added as grinding medium with the ratio to powders as of 1:2. The obtained powders were dried and then calcined at temperatures of 600, 700 and 800 °C, respectively. The objective of this research was to investigate the effects of calcination temperature on the properties of GDC10. The powders were characterized using XRF, TGA, XRD, and PSA instruments. XRF analysis shows the presence of Ce, Gd and O elements in stoichiometric composition without any impurities. XRD analysis showed single phase structure of CeO2 where the crystallite size and lattice parameter increases and decreases, respectively, as the calcination temperature increases. The smallest particle size of 647.3 nm was obtained at the calcination temperature of 600 °C. The density of all GDC10 samples sintered at 1350 °C was found to be higher than 95%. In addition, the calcination temperature also influenced the ionic conductivity where the highest obtained value was 0.0153 S.cm-1 at 800 °C for the sample calcinaed at 600 °C. The results suggest that the calcination temperature affected the properties of GDC10 for solid oxide fuel cell application. Penerbit Universiti Kebangsaan Malaysia 2020-12 Article PeerReviewed application/pdf en http://journalarticle.ukm.my/16183/1/30.pdf Damisih, and Hapsari, Ade Utami and Agustanhakri, and Deni, Yelvia and Arjasa, Oka Pradipta and Anggaravidya, Mahendra and Raharjo, Jarot and Mahendra Rao Somalu, (2020) Characteristics of gadolinium doped cerium at different calcination temperatures for intermediate temperature SOFC. Sains Malaysiana, 49 (12). pp. 3189-3196. ISSN 0126-6039 https://www.ukm.my/jsm/malay_journals/jilid49bil12_2020/KandunganJilid49Bil12_2020.html |
| spellingShingle | Damisih, Hapsari, Ade Utami Agustanhakri, Deni, Yelvia Arjasa, Oka Pradipta Anggaravidya, Mahendra Raharjo, Jarot Mahendra Rao Somalu, Characteristics of gadolinium doped cerium at different calcination temperatures for intermediate temperature SOFC |
| title | Characteristics of gadolinium doped cerium at different calcination temperatures for intermediate temperature SOFC |
| title_full | Characteristics of gadolinium doped cerium at different calcination temperatures for intermediate temperature SOFC |
| title_fullStr | Characteristics of gadolinium doped cerium at different calcination temperatures for intermediate temperature SOFC |
| title_full_unstemmed | Characteristics of gadolinium doped cerium at different calcination temperatures for intermediate temperature SOFC |
| title_short | Characteristics of gadolinium doped cerium at different calcination temperatures for intermediate temperature SOFC |
| title_sort | characteristics of gadolinium doped cerium at different calcination temperatures for intermediate temperature sofc |
| url | http://journalarticle.ukm.my/16183/1/30.pdf |
| work_keys_str_mv | AT damisih characteristicsofgadoliniumdopedceriumatdifferentcalcinationtemperaturesforintermediatetemperaturesofc AT hapsariadeutami characteristicsofgadoliniumdopedceriumatdifferentcalcinationtemperaturesforintermediatetemperaturesofc AT agustanhakri characteristicsofgadoliniumdopedceriumatdifferentcalcinationtemperaturesforintermediatetemperaturesofc AT deniyelvia characteristicsofgadoliniumdopedceriumatdifferentcalcinationtemperaturesforintermediatetemperaturesofc AT arjasaokapradipta characteristicsofgadoliniumdopedceriumatdifferentcalcinationtemperaturesforintermediatetemperaturesofc AT anggaravidyamahendra characteristicsofgadoliniumdopedceriumatdifferentcalcinationtemperaturesforintermediatetemperaturesofc AT raharjojarot characteristicsofgadoliniumdopedceriumatdifferentcalcinationtemperaturesforintermediatetemperaturesofc AT mahendraraosomalu characteristicsofgadoliniumdopedceriumatdifferentcalcinationtemperaturesforintermediatetemperaturesofc |