Preparation and characterization of carbon black diamond composite electrodes for anodic degradation of phenol
Carbon black diamond (CBD) composite electrodes have been prepared with different percentages of carbon black (5 (5CBD), 20 (20CBD) and 40 (40CBD) as the conductive agent. This article reports for the first time the electrochemical behavior of CBD electrodes. The electrochemical properties of these...
| প্রধান লেখক: | , , |
|---|---|
| বিন্যাস: | প্রবন্ধ |
| ভাষা: | English |
| প্রকাশিত: |
Elsevier
2015
|
| বিষয়গুলি: | |
| অনলাইন ব্যবহার করুন: | http://eprints.um.edu.my/13888/1/Preparation_and_characterization_of_carbon_black_diamond.pdf |
| _version_ | 1825720433248305152 |
|---|---|
| author | Ajeel, M.A. Aroua, M.K. Daud, W.M.A.W. |
| author_facet | Ajeel, M.A. Aroua, M.K. Daud, W.M.A.W. |
| author_sort | Ajeel, M.A. |
| collection | UM |
| description | Carbon black diamond (CBD) composite electrodes have been prepared with different percentages of carbon black (5 (5CBD), 20 (20CBD) and 40 (40CBD) as the conductive agent. This article reports for the first time the electrochemical behavior of CBD electrodes. The electrochemical properties of these three electrodes were characterized by cyclic voltammetry in 0.5 M H2SO4 and at 100 mV/s scanning rate. The working potential windows of 5CBD, 20CBD and 40CBD electrodes were 3.35, 2.4 and 1.75V vs. Ag/AgCl respectively. Anodic oxidation behavior of phenol was studied by cyclic voltammetry on CBD electrodes in aqueous solution of 0.5 M H2SO4, 0.5 M Na2SO4 and 0.5 M NaOH containing 500 mg/L phenol at 25 degrees C. The results indicated that the CBD electrodes were more active at low pH solution. The anodic oxidation of phenol led to the formation of passive adhesive film on CBD electrodes which reduced the peaks until a constant value of oxidation current was obtained. 20CBD electrode was selected to study the degradation of 500 mg/L phenol solution with pH 3 and pH 6 and applied current density of 50 mA/cm(2). The removal efficiency was more than 97 at pH 3. (C) 2014 Elsevier Ltd. All rights reserved. |
| first_indexed | 2024-03-06T05:35:04Z |
| format | Article |
| id | um.eprints-13888 |
| institution | Universiti Malaya |
| language | English |
| last_indexed | 2024-03-06T05:35:04Z |
| publishDate | 2015 |
| publisher | Elsevier |
| record_format | dspace |
| spelling | um.eprints-138882017-11-08T08:57:53Z http://eprints.um.edu.my/13888/ Preparation and characterization of carbon black diamond composite electrodes for anodic degradation of phenol Ajeel, M.A. Aroua, M.K. Daud, W.M.A.W. T Technology (General) TP Chemical technology Carbon black diamond (CBD) composite electrodes have been prepared with different percentages of carbon black (5 (5CBD), 20 (20CBD) and 40 (40CBD) as the conductive agent. This article reports for the first time the electrochemical behavior of CBD electrodes. The electrochemical properties of these three electrodes were characterized by cyclic voltammetry in 0.5 M H2SO4 and at 100 mV/s scanning rate. The working potential windows of 5CBD, 20CBD and 40CBD electrodes were 3.35, 2.4 and 1.75V vs. Ag/AgCl respectively. Anodic oxidation behavior of phenol was studied by cyclic voltammetry on CBD electrodes in aqueous solution of 0.5 M H2SO4, 0.5 M Na2SO4 and 0.5 M NaOH containing 500 mg/L phenol at 25 degrees C. The results indicated that the CBD electrodes were more active at low pH solution. The anodic oxidation of phenol led to the formation of passive adhesive film on CBD electrodes which reduced the peaks until a constant value of oxidation current was obtained. 20CBD electrode was selected to study the degradation of 500 mg/L phenol solution with pH 3 and pH 6 and applied current density of 50 mA/cm(2). The removal efficiency was more than 97 at pH 3. (C) 2014 Elsevier Ltd. All rights reserved. Elsevier 2015-01-20 Article PeerReviewed application/pdf en http://eprints.um.edu.my/13888/1/Preparation_and_characterization_of_carbon_black_diamond.pdf Ajeel, M.A. and Aroua, M.K. and Daud, W.M.A.W. (2015) Preparation and characterization of carbon black diamond composite electrodes for anodic degradation of phenol. Electrochimica Acta, 153. pp. 379-384. ISSN 0013-4686, DOI https://doi.org/10.1016/j.electacta.2014.11.163 <https://doi.org/10.1016/j.electacta.2014.11.163>. http://www.sciencedirect.com/science/article/pii/S0013468614023937 doi:10.1016/j.electacta.2014.11.163 |
| spellingShingle | T Technology (General) TP Chemical technology Ajeel, M.A. Aroua, M.K. Daud, W.M.A.W. Preparation and characterization of carbon black diamond composite electrodes for anodic degradation of phenol |
| title | Preparation and characterization of carbon black diamond composite electrodes for anodic degradation of phenol |
| title_full | Preparation and characterization of carbon black diamond composite electrodes for anodic degradation of phenol |
| title_fullStr | Preparation and characterization of carbon black diamond composite electrodes for anodic degradation of phenol |
| title_full_unstemmed | Preparation and characterization of carbon black diamond composite electrodes for anodic degradation of phenol |
| title_short | Preparation and characterization of carbon black diamond composite electrodes for anodic degradation of phenol |
| title_sort | preparation and characterization of carbon black diamond composite electrodes for anodic degradation of phenol |
| topic | T Technology (General) TP Chemical technology |
| url | http://eprints.um.edu.my/13888/1/Preparation_and_characterization_of_carbon_black_diamond.pdf |
| work_keys_str_mv | AT ajeelma preparationandcharacterizationofcarbonblackdiamondcompositeelectrodesforanodicdegradationofphenol AT arouamk preparationandcharacterizationofcarbonblackdiamondcompositeelectrodesforanodicdegradationofphenol AT daudwmaw preparationandcharacterizationofcarbonblackdiamondcompositeelectrodesforanodicdegradationofphenol |