Corrosion of carbon steel in aqueous carbonated solution of MEA/bmimDCA
Carbon steel corrosion rates were measured in carbonated solution mixtures of monoethanolamine (MEA) and 1-Butyl-3-methylimidazolium dicyandiamide (bmim DCA) and MEA without bmim DCA, using polarization curve and electrochemical impedance spectroscopy (EIS). Corrosion tests were carried out for 4.0...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Electrochemical Science Group
2011
|
| Subjects: | |
| Online Access: | http://eprints.um.edu.my/5754/1/Corrosion_of_Carbon_Steel_in_Aqueous_Carbonated_Solution_of_MEA%5Bbmim%5D%5BDCA%5D.pdf |
| _version_ | 1796945336844943360 |
|---|---|
| author | Hamah-Ali, Barham Ali, Brahim Si Yusoff, Rozita Aroua, Mohamed Kheireddine |
| author_facet | Hamah-Ali, Barham Ali, Brahim Si Yusoff, Rozita Aroua, Mohamed Kheireddine |
| author_sort | Hamah-Ali, Barham |
| collection | UM |
| description | Carbon steel corrosion rates were measured in carbonated solution mixtures of monoethanolamine (MEA) and 1-Butyl-3-methylimidazolium dicyandiamide (bmim DCA) and MEA without bmim DCA, using polarization curve and electrochemical impedance spectroscopy (EIS). Corrosion tests were carried out for 4.0 M carbonated MEA and bmim DCA concentration varied from 0.1 to 1.0 M. The CO2 loading was 0.55 mol/mol and temperature was varied from 40 to 80 oC. Results showed adding bmim DCA decreased the corrosion rate of carbon steel for 4.0 M MEA/ bmim DCA system. However, the effect of bmim DCA addition was less as the temperature increased to 80 oC. Scanning Electron Microscope (SEM) and Energy dispersive X-ray analysis (EDX) were also carried out to characterize the surface morphology and corrosion product formed on the electrode surface. The SEM and EDX spectrum showed that a protective corrosion layer was formed on the electrode surface for 4.0 M MEA/ bmim DCA system. The corrosion rate of carbon steel was also measured using EIS at 40 oC and 4.0 M MEA/ 1.0 M bmim DCA with different exposure times. It was found the corrosion rate increased at first, but decreased progressively with time. The results from EIS are consistent with those found from the polarization curve, SEM and EDX. |
| first_indexed | 2024-03-06T05:15:09Z |
| format | Article |
| id | um.eprints-5754 |
| institution | Universiti Malaya |
| language | English |
| last_indexed | 2024-03-06T05:15:09Z |
| publishDate | 2011 |
| publisher | Electrochemical Science Group |
| record_format | dspace |
| spelling | um.eprints-57542021-01-20T07:43:31Z http://eprints.um.edu.my/5754/ Corrosion of carbon steel in aqueous carbonated solution of MEA/bmimDCA Hamah-Ali, Barham Ali, Brahim Si Yusoff, Rozita Aroua, Mohamed Kheireddine TA Engineering (General). Civil engineering (General) Carbon steel corrosion rates were measured in carbonated solution mixtures of monoethanolamine (MEA) and 1-Butyl-3-methylimidazolium dicyandiamide (bmim DCA) and MEA without bmim DCA, using polarization curve and electrochemical impedance spectroscopy (EIS). Corrosion tests were carried out for 4.0 M carbonated MEA and bmim DCA concentration varied from 0.1 to 1.0 M. The CO2 loading was 0.55 mol/mol and temperature was varied from 40 to 80 oC. Results showed adding bmim DCA decreased the corrosion rate of carbon steel for 4.0 M MEA/ bmim DCA system. However, the effect of bmim DCA addition was less as the temperature increased to 80 oC. Scanning Electron Microscope (SEM) and Energy dispersive X-ray analysis (EDX) were also carried out to characterize the surface morphology and corrosion product formed on the electrode surface. The SEM and EDX spectrum showed that a protective corrosion layer was formed on the electrode surface for 4.0 M MEA/ bmim DCA system. The corrosion rate of carbon steel was also measured using EIS at 40 oC and 4.0 M MEA/ 1.0 M bmim DCA with different exposure times. It was found the corrosion rate increased at first, but decreased progressively with time. The results from EIS are consistent with those found from the polarization curve, SEM and EDX. Electrochemical Science Group 2011 Article PeerReviewed application/pdf en http://eprints.um.edu.my/5754/1/Corrosion_of_Carbon_Steel_in_Aqueous_Carbonated_Solution_of_MEA%5Bbmim%5D%5BDCA%5D.pdf Hamah-Ali, Barham and Ali, Brahim Si and Yusoff, Rozita and Aroua, Mohamed Kheireddine (2011) Corrosion of carbon steel in aqueous carbonated solution of MEA/bmimDCA. International Journal of Electrochemical Science, 6. pp. 181-198. ISSN 1452-3981, http://www.electrochemsci.org/papers/vol6/6010181.pdf |
| spellingShingle | TA Engineering (General). Civil engineering (General) Hamah-Ali, Barham Ali, Brahim Si Yusoff, Rozita Aroua, Mohamed Kheireddine Corrosion of carbon steel in aqueous carbonated solution of MEA/bmimDCA |
| title | Corrosion of carbon steel in aqueous carbonated solution of MEA/bmimDCA |
| title_full | Corrosion of carbon steel in aqueous carbonated solution of MEA/bmimDCA |
| title_fullStr | Corrosion of carbon steel in aqueous carbonated solution of MEA/bmimDCA |
| title_full_unstemmed | Corrosion of carbon steel in aqueous carbonated solution of MEA/bmimDCA |
| title_short | Corrosion of carbon steel in aqueous carbonated solution of MEA/bmimDCA |
| title_sort | corrosion of carbon steel in aqueous carbonated solution of mea bmimdca |
| topic | TA Engineering (General). Civil engineering (General) |
| url | http://eprints.um.edu.my/5754/1/Corrosion_of_Carbon_Steel_in_Aqueous_Carbonated_Solution_of_MEA%5Bbmim%5D%5BDCA%5D.pdf |
| work_keys_str_mv | AT hamahalibarham corrosionofcarbonsteelinaqueouscarbonatedsolutionofmeabmimdca AT alibrahimsi corrosionofcarbonsteelinaqueouscarbonatedsolutionofmeabmimdca AT yusoffrozita corrosionofcarbonsteelinaqueouscarbonatedsolutionofmeabmimdca AT arouamohamedkheireddine corrosionofcarbonsteelinaqueouscarbonatedsolutionofmeabmimdca |