Degradation study on ternary zinc magnesium phosphate glasses
Glasses with composition (ZnO)30(MgO) x (P2O5)70−x (x = 5, 8, 10, 13, 15, 18, and 20 mol.%) have been successfully prepared by the melt-quenching technique. Degradation study has been carried out by means of measuring their chemical durability against buffer solutions with initial pH values of 4.01,...
| المؤلفون الرئيسيون: | , , , |
|---|---|
| التنسيق: | مقال |
| اللغة: | English |
| منشور في: |
Springer
2011
|
| الوصول للمادة أونلاين: | http://psasir.upm.edu.my/id/eprint/25138/1/Degradation%20study%20on%20ternary%20zinc%20magnesium%20phosphate%20glasses.pdf |
| _version_ | 1825925716719435776 |
|---|---|
| author | Khor, Shing Fhan Talib, Zainal Abidin Wan Yusoff, Wan Mohamad Daud Abd. Aziz, Sidek |
| author_facet | Khor, Shing Fhan Talib, Zainal Abidin Wan Yusoff, Wan Mohamad Daud Abd. Aziz, Sidek |
| author_sort | Khor, Shing Fhan |
| collection | UPM |
| description | Glasses with composition (ZnO)30(MgO) x (P2O5)70−x (x = 5, 8, 10, 13, 15, 18, and 20 mol.%) have been successfully prepared by the melt-quenching technique. Degradation study has been carried out by means of measuring their chemical durability against buffer solutions with initial pH values of 4.01, 7.00, and 10.01 at an ambient temperature for up to 30 days. The dissolution rate (D R) was obtained by calculating the measured weight loss of the glasses per unit surface area per unit immersion time. The results show that the glasses have better corrosion resistance in basic solution. It was also found that the weight loss is related to the MgO concentration with lower P2O5 concentration exhibiting greater corrosion resistance irrespective of acidic, neutral, or basic solutions as immersion liquid. All the sample surfaces and edges were corroded and the solutions experienced a decrease in pH values during the duration of the corrosion test. |
| first_indexed | 2024-03-06T08:01:56Z |
| format | Article |
| id | upm.eprints-25138 |
| institution | Universiti Putra Malaysia |
| language | English |
| last_indexed | 2024-03-06T08:01:56Z |
| publishDate | 2011 |
| publisher | Springer |
| record_format | dspace |
| spelling | upm.eprints-251382019-12-16T08:37:57Z http://psasir.upm.edu.my/id/eprint/25138/ Degradation study on ternary zinc magnesium phosphate glasses Khor, Shing Fhan Talib, Zainal Abidin Wan Yusoff, Wan Mohamad Daud Abd. Aziz, Sidek Glasses with composition (ZnO)30(MgO) x (P2O5)70−x (x = 5, 8, 10, 13, 15, 18, and 20 mol.%) have been successfully prepared by the melt-quenching technique. Degradation study has been carried out by means of measuring their chemical durability against buffer solutions with initial pH values of 4.01, 7.00, and 10.01 at an ambient temperature for up to 30 days. The dissolution rate (D R) was obtained by calculating the measured weight loss of the glasses per unit surface area per unit immersion time. The results show that the glasses have better corrosion resistance in basic solution. It was also found that the weight loss is related to the MgO concentration with lower P2O5 concentration exhibiting greater corrosion resistance irrespective of acidic, neutral, or basic solutions as immersion liquid. All the sample surfaces and edges were corroded and the solutions experienced a decrease in pH values during the duration of the corrosion test. Springer 2011-12 Article PeerReviewed application/pdf en http://psasir.upm.edu.my/id/eprint/25138/1/Degradation%20study%20on%20ternary%20zinc%20magnesium%20phosphate%20glasses.pdf Khor, Shing Fhan and Talib, Zainal Abidin and Wan Yusoff, Wan Mohamad Daud and Abd. Aziz, Sidek (2011) Degradation study on ternary zinc magnesium phosphate glasses. Journal of Materials Science, 46 (24). pp. 7895-7900. ISSN 0022-2461; ESSN: 1573-4803 https://link.springer.com/article/10.1007/s10853-011-5777-0 10.1007/s10853-011-5777-0 |
| spellingShingle | Khor, Shing Fhan Talib, Zainal Abidin Wan Yusoff, Wan Mohamad Daud Abd. Aziz, Sidek Degradation study on ternary zinc magnesium phosphate glasses |
| title | Degradation study on ternary zinc magnesium phosphate glasses |
| title_full | Degradation study on ternary zinc magnesium phosphate glasses |
| title_fullStr | Degradation study on ternary zinc magnesium phosphate glasses |
| title_full_unstemmed | Degradation study on ternary zinc magnesium phosphate glasses |
| title_short | Degradation study on ternary zinc magnesium phosphate glasses |
| title_sort | degradation study on ternary zinc magnesium phosphate glasses |
| url | http://psasir.upm.edu.my/id/eprint/25138/1/Degradation%20study%20on%20ternary%20zinc%20magnesium%20phosphate%20glasses.pdf |
| work_keys_str_mv | AT khorshingfhan degradationstudyonternaryzincmagnesiumphosphateglasses AT talibzainalabidin degradationstudyonternaryzincmagnesiumphosphateglasses AT wanyusoffwanmohamaddaud degradationstudyonternaryzincmagnesiumphosphateglasses AT abdazizsidek degradationstudyonternaryzincmagnesiumphosphateglasses |