Rubber Blend (ENR25/NBR) Based Pressure-Sensitive Adhesives
In this study, the synthesis and characterization of epoxidized natural rubber (ENR 25)/ acrylonitrile-butadiene rubber (NBR) blend pressure sensitive adhesive (PSA) were presented. The blend ratio of ENR25/NBR was fixed at 0, 20, 40, 60, 80, and 100% of ENR 25 content. The zinc oxide (ZnO) and magn...
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English |
| Published: |
2017
|
| Subjects: | |
| Online Access: | http://eprints.usm.my/45491/1/SOO%20KAI%20WAI.pdf |
| _version_ | 1797011387878211584 |
|---|---|
| author | Soo, Kai Wai |
| author_facet | Soo, Kai Wai |
| author_sort | Soo, Kai Wai |
| collection | USM |
| description | In this study, the synthesis and characterization of epoxidized natural rubber (ENR 25)/ acrylonitrile-butadiene rubber (NBR) blend pressure sensitive adhesive (PSA) were presented. The blend ratio of ENR25/NBR was fixed at 0, 20, 40, 60, 80, and 100% of ENR 25 content. The zinc oxide (ZnO) and magnesium oxide (MgO) were used as a reinforcing filler to prepare the composite adhesive. Five different loadings, i.e. 10, 20, 30, 40 and 50 phr filler was used in the adhesive formulation. The benzoyl peroxide (BPO) is used as a crosslinking agent to prepare the crosslinked adhesive. The loading of benzoyl peroxide was varied from 1 to 5 phr. Toluene was used as solvent throughout the study. |
| first_indexed | 2024-03-06T15:33:37Z |
| format | Thesis |
| id | usm.eprints-45491 |
| institution | Universiti Sains Malaysia |
| language | English |
| last_indexed | 2024-03-06T15:33:37Z |
| publishDate | 2017 |
| record_format | dspace |
| spelling | usm.eprints-454912019-09-19T06:47:03Z http://eprints.usm.my/45491/ Rubber Blend (ENR25/NBR) Based Pressure-Sensitive Adhesives Soo, Kai Wai T1-995 Technology(General) In this study, the synthesis and characterization of epoxidized natural rubber (ENR 25)/ acrylonitrile-butadiene rubber (NBR) blend pressure sensitive adhesive (PSA) were presented. The blend ratio of ENR25/NBR was fixed at 0, 20, 40, 60, 80, and 100% of ENR 25 content. The zinc oxide (ZnO) and magnesium oxide (MgO) were used as a reinforcing filler to prepare the composite adhesive. Five different loadings, i.e. 10, 20, 30, 40 and 50 phr filler was used in the adhesive formulation. The benzoyl peroxide (BPO) is used as a crosslinking agent to prepare the crosslinked adhesive. The loading of benzoyl peroxide was varied from 1 to 5 phr. Toluene was used as solvent throughout the study. 2017-07 Thesis NonPeerReviewed application/pdf en http://eprints.usm.my/45491/1/SOO%20KAI%20WAI.pdf Soo, Kai Wai (2017) Rubber Blend (ENR25/NBR) Based Pressure-Sensitive Adhesives. PhD thesis, Universiti Sains Malaysia. |
| spellingShingle | T1-995 Technology(General) Soo, Kai Wai Rubber Blend (ENR25/NBR) Based Pressure-Sensitive Adhesives |
| title | Rubber Blend (ENR25/NBR) Based Pressure-Sensitive Adhesives |
| title_full | Rubber Blend (ENR25/NBR) Based Pressure-Sensitive Adhesives |
| title_fullStr | Rubber Blend (ENR25/NBR) Based Pressure-Sensitive Adhesives |
| title_full_unstemmed | Rubber Blend (ENR25/NBR) Based Pressure-Sensitive Adhesives |
| title_short | Rubber Blend (ENR25/NBR) Based Pressure-Sensitive Adhesives |
| title_sort | rubber blend enr25 nbr based pressure sensitive adhesives |
| topic | T1-995 Technology(General) |
| url | http://eprints.usm.my/45491/1/SOO%20KAI%20WAI.pdf |
| work_keys_str_mv | AT sookaiwai rubberblendenr25nbrbasedpressuresensitiveadhesives |