Preparation Of Activated Carbon From Bamboo Stem Using Microwave Irradiation For Methylene Blue Dye Removal From Aqueous Solution
A batch process was used to investigate the adsorption of the methylene blue (MB) dye onto bamboo stem based activated carbon (BSAC). In order to prepare the BSAC, bamboo stem (BS) undergoes physical activation process which involves microwave irradiation and carbon dioxide (CO2) gasification. By...
| Main Author: | |
|---|---|
| Format: | Monograph |
| Language: | English |
| Published: |
Universiti Sains Malaysia
2018
|
| Subjects: | |
| Online Access: | http://eprints.usm.my/54042/1/Preparation%20Of%20Activated%20Carbon%20From%20Bamboo%20Stem%20Using%20Microwave%20Irradiation%20For%20Methylene%20Blue%20Dye%20Removal%20From%20Aqueous%20Solution_Navenprasath%20Sandrasegaran_K4_2018.pdf |
| _version_ | 1797013142331457536 |
|---|---|
| author | Sandrasegaran, Navenprasath |
| author_facet | Sandrasegaran, Navenprasath |
| author_sort | Sandrasegaran, Navenprasath |
| collection | USM |
| description | A batch process was used to investigate the adsorption of the methylene blue (MB) dye onto bamboo stem based activated carbon (BSAC). In order to prepare the BSAC, bamboo stem (BS) undergoes physical activation process which involves microwave
irradiation and carbon dioxide (CO2) gasification. By using response surface methodology (RSM), the optimum preparation conditions were obtained at microwave power and activation time of 440 W and 6.00 minutes respectively which resulted
88.27% MB removal. The optimized sample has high surface area (636.48 m2/g), pore volume (0.4558 cm2/g) and fixed carbon content (75.34%). The pore of BSAC was mesoporous type with average pore diameter of 2.75nm. The effect of initial dye
concentration (25-300 mg/L), contact time (0-24 hours) and solution temperature (30-60⁰ C) were also evaluated through. The obtained equilibrium data for MB adsorption by
BSAC dye was best fitted by Langmuir model with monolayer maximum adsorption capacity of 222.22 mg/g. Meanwhile, the kinetics data was best represented by the pseudo second-order model. The adsorption process of MB onto BSAC was endothermic
and spontaneous process. |
| first_indexed | 2024-03-06T15:57:54Z |
| format | Monograph |
| id | usm.eprints-54042 |
| institution | Universiti Sains Malaysia |
| language | English |
| last_indexed | 2024-03-06T15:57:54Z |
| publishDate | 2018 |
| publisher | Universiti Sains Malaysia |
| record_format | dspace |
| spelling | usm.eprints-540422022-08-15T02:53:28Z http://eprints.usm.my/54042/ Preparation Of Activated Carbon From Bamboo Stem Using Microwave Irradiation For Methylene Blue Dye Removal From Aqueous Solution Sandrasegaran, Navenprasath T Technology TP Chemical Technology A batch process was used to investigate the adsorption of the methylene blue (MB) dye onto bamboo stem based activated carbon (BSAC). In order to prepare the BSAC, bamboo stem (BS) undergoes physical activation process which involves microwave irradiation and carbon dioxide (CO2) gasification. By using response surface methodology (RSM), the optimum preparation conditions were obtained at microwave power and activation time of 440 W and 6.00 minutes respectively which resulted 88.27% MB removal. The optimized sample has high surface area (636.48 m2/g), pore volume (0.4558 cm2/g) and fixed carbon content (75.34%). The pore of BSAC was mesoporous type with average pore diameter of 2.75nm. The effect of initial dye concentration (25-300 mg/L), contact time (0-24 hours) and solution temperature (30-60⁰ C) were also evaluated through. The obtained equilibrium data for MB adsorption by BSAC dye was best fitted by Langmuir model with monolayer maximum adsorption capacity of 222.22 mg/g. Meanwhile, the kinetics data was best represented by the pseudo second-order model. The adsorption process of MB onto BSAC was endothermic and spontaneous process. Universiti Sains Malaysia 2018-06-01 Monograph NonPeerReviewed application/pdf en http://eprints.usm.my/54042/1/Preparation%20Of%20Activated%20Carbon%20From%20Bamboo%20Stem%20Using%20Microwave%20Irradiation%20For%20Methylene%20Blue%20Dye%20Removal%20From%20Aqueous%20Solution_Navenprasath%20Sandrasegaran_K4_2018.pdf Sandrasegaran, Navenprasath (2018) Preparation Of Activated Carbon From Bamboo Stem Using Microwave Irradiation For Methylene Blue Dye Removal From Aqueous Solution. Project Report. Universiti Sains Malaysia, Pusat Pengajian Kejuruteraan Kimia. (Submitted) |
| spellingShingle | T Technology TP Chemical Technology Sandrasegaran, Navenprasath Preparation Of Activated Carbon From Bamboo Stem Using Microwave Irradiation For Methylene Blue Dye Removal From Aqueous Solution |
| title | Preparation Of Activated Carbon From Bamboo Stem Using Microwave Irradiation For Methylene Blue Dye Removal From Aqueous Solution |
| title_full | Preparation Of Activated Carbon From Bamboo Stem Using Microwave Irradiation For Methylene Blue Dye Removal From Aqueous Solution |
| title_fullStr | Preparation Of Activated Carbon From Bamboo Stem Using Microwave Irradiation For Methylene Blue Dye Removal From Aqueous Solution |
| title_full_unstemmed | Preparation Of Activated Carbon From Bamboo Stem Using Microwave Irradiation For Methylene Blue Dye Removal From Aqueous Solution |
| title_short | Preparation Of Activated Carbon From Bamboo Stem Using Microwave Irradiation For Methylene Blue Dye Removal From Aqueous Solution |
| title_sort | preparation of activated carbon from bamboo stem using microwave irradiation for methylene blue dye removal from aqueous solution |
| topic | T Technology TP Chemical Technology |
| url | http://eprints.usm.my/54042/1/Preparation%20Of%20Activated%20Carbon%20From%20Bamboo%20Stem%20Using%20Microwave%20Irradiation%20For%20Methylene%20Blue%20Dye%20Removal%20From%20Aqueous%20Solution_Navenprasath%20Sandrasegaran_K4_2018.pdf |
| work_keys_str_mv | AT sandrasegarannavenprasath preparationofactivatedcarbonfrombamboostemusingmicrowaveirradiationformethylenebluedyeremovalfromaqueoussolution |