Biocompatibility Of Electrospun Bombyx Mori Silk Fibroin With Poly(3-Hydroxybutyrate-Co-3-Hydroxyhexanoate) As A Biomaterial For Tissue-Engineered Scaffolds
Polyhydroxyalkanoates (PHAs) are polyesters produced by microorganisms under unbalanced growth conditions. They are well documented as a biodegradable and biocompatible polymer, making them attractive as biomaterials for applications in tissue engineering. Poly(3-hydroxybutyrate-co-3-hydroxyhexanoat...
Main Author: | Ang, Shaik Ling |
---|---|
Format: | Thesis |
Language: | English |
Published: |
2019
|
Subjects: | |
Online Access: | http://eprints.usm.my/55696/1/24%20Pages%20from%20Ang%20Shaik%20Ling.pdf |
Similar Items
-
Preparation And Characterization Of Poly(3-Hydroxybutyrate-Co-3- Hydroxyhexanoate) Reinforced Kenaf Fibre
by: Lee, Joyyi
Published: (2017) -
Fabrication And Characterization Of Poly(3-Hydroxybutyrate-Co-4- Hydroxybutyrate)/Chitosan Blend And Its Silver Nanocomposite Material
by: Mathava, Rennukka
Published: (2014) -
Biosynthesis And Characterization Of Poly(3-Hydroxybutyrate-Co-4-Hydroxybutyrate) Copolymer From Cupriavidus Sp. Usmahm13
by: Ramachandran, Hema
Published: (2013) -
Biosynthesis And Characterization Of Poly(3-Hydroxybutyrate-Co-3- Hydroxyvalerate) From Cupriavidus Malaysiensis Usmaa1020
Using Glycerin Pitch As Main Carbon Source
by: Rozina, Rozina
Published: (2022) -
Review on Fabrication and Application of Regenerated Bombyx mori Silk Fibroin Materials
by: Wang Ke, et al.
Published: (2023-06-01)