Nio Modification Using Zr4+ And Ca2+ For Dielectric Improvement
In this research, the effect of Zirconium ions (Zr4+) and Calcium ions (Ca2+) dopant on NiO was investigated. The electroceramic of Ni(l_;c)ZrxO, Ni(l_x)CaxO and Nio.9SZrO.o2CaO.OI was prepared by using solid state reaction method. Three main raw materials ofNiO, Zr02 and CaO were mixed for 24 ho...
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English |
| Published: |
2014
|
| Subjects: | |
| Online Access: | http://eprints.usm.my/61091/1/24%20Pages%20from%2000001780807.pdf |
| Summary: | In this research, the effect of Zirconium ions (Zr4+) and Calcium ions (Ca2+)
dopant on NiO was investigated. The electroceramic of Ni(l_;c)ZrxO, Ni(l_x)CaxO and
Nio.9SZrO.o2CaO.OI was prepared by using solid state reaction method. Three main raw
materials ofNiO, Zr02 and CaO were mixed for 24 hours, then were calcined at 1000°C.
Ni(l_x)Zr. |
|---|