Effect of austempering holding time variations of 30, 60 and 90 minutes at 300 oc on the microstructure and toughness of nodular cast iron
The phases of the nodular cast iron matrix are similar to those of steel. Therefore, heat treatment of steel can be applied to nodular cast iron. A potential heat treatment for nodular cast iron is austempering. This study aimed to determine the effect of austempering holding time at 300 oC on th...
| Main Authors: | , , , , |
|---|---|
| Format: | Conference or Workshop Item |
| Language: | English |
| Published: |
2023
|
| Subjects: | |
| Online Access: | http://eprints.uthm.edu.my/11704/1/P16754_131643e2d80aa7bdd9c01976dae6eaff%201.pdf |
| _version_ | 1817857239707287552 |
|---|---|
| author | Darmawan, A S Anggono, A D Yulianto, A Febriantoko, B W Hamid, A |
| author_facet | Darmawan, A S Anggono, A D Yulianto, A Febriantoko, B W Hamid, A |
| author_sort | Darmawan, A S |
| collection | UTHM |
| description | The phases of the nodular cast iron matrix are similar to those of steel. Therefore, heat
treatment of steel can be applied to nodular cast iron. A potential heat treatment for nodular cast
iron is austempering. This study aimed to determine the effect of austempering holding time at
300 oC on the microstructure and toughness of nodular cast iron. The austempering process
begins with austenitizing at a temperature of 850 oC for 60 minutes, then the quenching process
is carried out in a salt bath until a temperature of 300 oC is held with variations of 30, 60, and 90
minutes, then cooled to room temperature. Metallographic testing was conducted to determine
the phase change before and after the austempering process using a Scanning Electron
Microscope (SEM). Meanwhile, impact testing was carried out to determine changes in
toughness before and after the austempering process. At a holding time of 30 minutes,
metallographic testing on the raw material produced a gray coarse pearlite phase, black nodular
graphite surrounded by white ferrite. After the austempering process, gray fine pearlite and black
nodular graphite appeared. At the holding time of 60 and 90 minutes, the graphite sizes were
bigger. Austempering withholding times of 30, 60, and 90 minutes resulted in impact energy of
4.2, 10, and 11 Joule. From the results of the study, it was concluded that an increase in holding
time would increase the size of the graphite and the toughness of nodular cast iron. |
| first_indexed | 2024-12-08T07:42:40Z |
| format | Conference or Workshop Item |
| id | uthm.eprints-11704 |
| institution | Universiti Tun Hussein Onn Malaysia |
| language | English |
| last_indexed | 2024-12-08T07:42:40Z |
| publishDate | 2023 |
| record_format | dspace |
| spelling | uthm.eprints-117042024-11-27T03:19:34Z http://eprints.uthm.edu.my/11704/ Effect of austempering holding time variations of 30, 60 and 90 minutes at 300 oc on the microstructure and toughness of nodular cast iron Darmawan, A S Anggono, A D Yulianto, A Febriantoko, B W Hamid, A TA401-492 Materials of engineering and construction. Mechanics of materials The phases of the nodular cast iron matrix are similar to those of steel. Therefore, heat treatment of steel can be applied to nodular cast iron. A potential heat treatment for nodular cast iron is austempering. This study aimed to determine the effect of austempering holding time at 300 oC on the microstructure and toughness of nodular cast iron. The austempering process begins with austenitizing at a temperature of 850 oC for 60 minutes, then the quenching process is carried out in a salt bath until a temperature of 300 oC is held with variations of 30, 60, and 90 minutes, then cooled to room temperature. Metallographic testing was conducted to determine the phase change before and after the austempering process using a Scanning Electron Microscope (SEM). Meanwhile, impact testing was carried out to determine changes in toughness before and after the austempering process. At a holding time of 30 minutes, metallographic testing on the raw material produced a gray coarse pearlite phase, black nodular graphite surrounded by white ferrite. After the austempering process, gray fine pearlite and black nodular graphite appeared. At the holding time of 60 and 90 minutes, the graphite sizes were bigger. Austempering withholding times of 30, 60, and 90 minutes resulted in impact energy of 4.2, 10, and 11 Joule. From the results of the study, it was concluded that an increase in holding time would increase the size of the graphite and the toughness of nodular cast iron. 2023-10-13 Conference or Workshop Item PeerReviewed text en http://eprints.uthm.edu.my/11704/1/P16754_131643e2d80aa7bdd9c01976dae6eaff%201.pdf Darmawan, A S and Anggono, A D and Yulianto, A and Febriantoko, B W and Hamid, A (2023) Effect of austempering holding time variations of 30, 60 and 90 minutes at 300 oc on the microstructure and toughness of nodular cast iron. In: ISAIME DEPARTEMEN TEKNIK MESIN UNIVERSITAS HASANUDDIN. http://10.1088/1742-6596/2739/1/012029 |
| spellingShingle | TA401-492 Materials of engineering and construction. Mechanics of materials Darmawan, A S Anggono, A D Yulianto, A Febriantoko, B W Hamid, A Effect of austempering holding time variations of 30, 60 and 90 minutes at 300 oc on the microstructure and toughness of nodular cast iron |
| title | Effect of austempering holding time variations of 30, 60 and 90 minutes at 300 oc on the microstructure and toughness of nodular cast iron |
| title_full | Effect of austempering holding time variations of 30, 60 and 90 minutes at 300 oc on the microstructure and toughness of nodular cast iron |
| title_fullStr | Effect of austempering holding time variations of 30, 60 and 90 minutes at 300 oc on the microstructure and toughness of nodular cast iron |
| title_full_unstemmed | Effect of austempering holding time variations of 30, 60 and 90 minutes at 300 oc on the microstructure and toughness of nodular cast iron |
| title_short | Effect of austempering holding time variations of 30, 60 and 90 minutes at 300 oc on the microstructure and toughness of nodular cast iron |
| title_sort | effect of austempering holding time variations of 30 60 and 90 minutes at 300 oc on the microstructure and toughness of nodular cast iron |
| topic | TA401-492 Materials of engineering and construction. Mechanics of materials |
| url | http://eprints.uthm.edu.my/11704/1/P16754_131643e2d80aa7bdd9c01976dae6eaff%201.pdf |
| work_keys_str_mv | AT darmawanas effectofaustemperingholdingtimevariationsof3060and90minutesat300oconthemicrostructureandtoughnessofnodularcastiron AT anggonoad effectofaustemperingholdingtimevariationsof3060and90minutesat300oconthemicrostructureandtoughnessofnodularcastiron AT yuliantoa effectofaustemperingholdingtimevariationsof3060and90minutesat300oconthemicrostructureandtoughnessofnodularcastiron AT febriantokobw effectofaustemperingholdingtimevariationsof3060and90minutesat300oconthemicrostructureandtoughnessofnodularcastiron AT hamida effectofaustemperingholdingtimevariationsof3060and90minutesat300oconthemicrostructureandtoughnessofnodularcastiron |