Water permeability of foamed concrete
This study focused on the compressive strength and water permeability of foamed concrete. Two types of foamed concrete mix with density 1500 kg/m3 and 1700 >5 kg/m were experimented Timber industrial ash (HA) were used as the partial cement replacement material, replacing 10% of Ordinary Port...
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English English English |
| Published: |
2004
|
| Subjects: | |
| Online Access: | http://eprints.uthm.edu.my/8652/1/24p%20MOHD%20HAZIMAN%20WAN%20IBRAHIM.pdf http://eprints.uthm.edu.my/8652/2/MOHD%20HAZIMAN%20WAN%20IBRAHIM%20COPYRIGHT%20DECLARATION.pdf http://eprints.uthm.edu.my/8652/3/MOHD%20HAZIMAN%20WAN%20IBRAHIM%20WATERMARK.pdf |
| _version_ | 1796869806962507776 |
|---|---|
| author | Wan Ibrahim, Mohd Haziman |
| author_facet | Wan Ibrahim, Mohd Haziman |
| author_sort | Wan Ibrahim, Mohd Haziman |
| collection | UTHM |
| description | This study focused on the compressive strength and water permeability of
foamed concrete. Two types of foamed concrete mix with density 1500 kg/m3 and 1700
>5
kg/m were experimented Timber industrial ash (HA) were used as the partial cement
replacement material, replacing 10% of Ordinary Portland cement (OPC) in the mix
design. The test cubes were 150 mm X 150 mm X150 mm size subjected to wet-cured
and air cured for up to 28 days. The density, compressive strength development and
water permeability of the TIA foamed concrete were determined to compare with the
control mix (without TIA). The test method adopted based on DIN 1048 was used to
determine the water permeability of foamed concrete at 28 days. Compressive strength
was determined at 3 days, 7 days and 28 days. It was found that the air-cured specimens
achieved a higher compressive strength and lower water permeability compared with the
wet-cured specimens. Foamed concrete with 10% HA reduced the water permeability
with a lower compressive strength at 28 days. The preliminary result indicated that HA
has potential to reduce the water permeability of foamed concrete. |
| first_indexed | 2024-03-05T22:00:16Z |
| format | Thesis |
| id | uthm.eprints-8652 |
| institution | Universiti Tun Hussein Onn Malaysia |
| language | English English English |
| last_indexed | 2024-03-05T22:00:16Z |
| publishDate | 2004 |
| record_format | dspace |
| spelling | uthm.eprints-86522023-05-02T02:13:07Z http://eprints.uthm.edu.my/8652/ Water permeability of foamed concrete Wan Ibrahim, Mohd Haziman TA Engineering (General). Civil engineering (General) TA401-492 Materials of engineering and construction. Mechanics of materials This study focused on the compressive strength and water permeability of foamed concrete. Two types of foamed concrete mix with density 1500 kg/m3 and 1700 >5 kg/m were experimented Timber industrial ash (HA) were used as the partial cement replacement material, replacing 10% of Ordinary Portland cement (OPC) in the mix design. The test cubes were 150 mm X 150 mm X150 mm size subjected to wet-cured and air cured for up to 28 days. The density, compressive strength development and water permeability of the TIA foamed concrete were determined to compare with the control mix (without TIA). The test method adopted based on DIN 1048 was used to determine the water permeability of foamed concrete at 28 days. Compressive strength was determined at 3 days, 7 days and 28 days. It was found that the air-cured specimens achieved a higher compressive strength and lower water permeability compared with the wet-cured specimens. Foamed concrete with 10% HA reduced the water permeability with a lower compressive strength at 28 days. The preliminary result indicated that HA has potential to reduce the water permeability of foamed concrete. 2004-04 Thesis NonPeerReviewed text en http://eprints.uthm.edu.my/8652/1/24p%20MOHD%20HAZIMAN%20WAN%20IBRAHIM.pdf text en http://eprints.uthm.edu.my/8652/2/MOHD%20HAZIMAN%20WAN%20IBRAHIM%20COPYRIGHT%20DECLARATION.pdf text en http://eprints.uthm.edu.my/8652/3/MOHD%20HAZIMAN%20WAN%20IBRAHIM%20WATERMARK.pdf Wan Ibrahim, Mohd Haziman (2004) Water permeability of foamed concrete. Masters thesis, Kolej Universiti Teknologi Tun Hussein Onn. |
| spellingShingle | TA Engineering (General). Civil engineering (General) TA401-492 Materials of engineering and construction. Mechanics of materials Wan Ibrahim, Mohd Haziman Water permeability of foamed concrete |
| title | Water permeability of foamed concrete |
| title_full | Water permeability of foamed concrete |
| title_fullStr | Water permeability of foamed concrete |
| title_full_unstemmed | Water permeability of foamed concrete |
| title_short | Water permeability of foamed concrete |
| title_sort | water permeability of foamed concrete |
| topic | TA Engineering (General). Civil engineering (General) TA401-492 Materials of engineering and construction. Mechanics of materials |
| url | http://eprints.uthm.edu.my/8652/1/24p%20MOHD%20HAZIMAN%20WAN%20IBRAHIM.pdf http://eprints.uthm.edu.my/8652/2/MOHD%20HAZIMAN%20WAN%20IBRAHIM%20COPYRIGHT%20DECLARATION.pdf http://eprints.uthm.edu.my/8652/3/MOHD%20HAZIMAN%20WAN%20IBRAHIM%20WATERMARK.pdf |
| work_keys_str_mv | AT wanibrahimmohdhaziman waterpermeabilityoffoamedconcrete |