MmNi5 and MmNi4.85Fe0.15 as Hydrogen Storage Medium
The characteristics of MmNi5 and MmNi4.85Fe0.15 in storing hydrogen gas were examined in this study. The absorption capacity of the metal was monitored under the influence of temperature and pressure. Due to the limitation on its operating conditions, the range of the temperature chosen was from 298...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Penerbit UTM Press
2001
|
| Subjects: | |
| Online Access: | http://eprints.utm.my/1516/1/JT35F1.pdf |
| _version_ | 1796853262171766784 |
|---|---|
| author | Johari, Anwar Mohd. Yunus, Rosli Noordin, Mohd. Suffian Md. Ghazali, Mohd. Nazlee Faisal Tuan Abdullah, Tuan Amran |
| author_facet | Johari, Anwar Mohd. Yunus, Rosli Noordin, Mohd. Suffian Md. Ghazali, Mohd. Nazlee Faisal Tuan Abdullah, Tuan Amran |
| author_sort | Johari, Anwar |
| collection | ePrints |
| description | The characteristics of MmNi5 and MmNi4.85Fe0.15 in storing hydrogen gas were examined in this study. The absorption capacity of the metal was monitored under the influence of temperature and pressure. Due to the limitation on its operating conditions, the range of the temperature chosen was from 298K to 323K while pressure was varied from 2 to 30 bar. Study conducted on MmNi5, showed that the amount of hydrogen absorbed was inversely proportional to the operating temperature. In the study of MnNi5 the maximum absorption was achieved at 298K and exhibited the plateau pressure of 10 bar. The hydrogen content was expressed as weight and the value was calculated to be at 1.20 wt%. As for MmNi5 at 313K abd 323K, the results are pointed at 0.9 wt% and 0.8 wt% whilst the plateau was encountedered at 20 and 24 bar, respectively. Study conducted on MmNi4.85Fe0.15 showed inconsistent findings with theory. After thorough examination, it was realized that the misbehavior of the sample was due to the insufficient agrresiveness activations method employed. |
| first_indexed | 2024-03-05T17:56:52Z |
| format | Article |
| id | utm.eprints-1516 |
| institution | Universiti Teknologi Malaysia - ePrints |
| language | English |
| last_indexed | 2024-03-05T17:56:52Z |
| publishDate | 2001 |
| publisher | Penerbit UTM Press |
| record_format | dspace |
| spelling | utm.eprints-15162017-11-01T04:17:46Z http://eprints.utm.my/1516/ MmNi5 and MmNi4.85Fe0.15 as Hydrogen Storage Medium Johari, Anwar Mohd. Yunus, Rosli Noordin, Mohd. Suffian Md. Ghazali, Mohd. Nazlee Faisal Tuan Abdullah, Tuan Amran TP Chemical technology The characteristics of MmNi5 and MmNi4.85Fe0.15 in storing hydrogen gas were examined in this study. The absorption capacity of the metal was monitored under the influence of temperature and pressure. Due to the limitation on its operating conditions, the range of the temperature chosen was from 298K to 323K while pressure was varied from 2 to 30 bar. Study conducted on MmNi5, showed that the amount of hydrogen absorbed was inversely proportional to the operating temperature. In the study of MnNi5 the maximum absorption was achieved at 298K and exhibited the plateau pressure of 10 bar. The hydrogen content was expressed as weight and the value was calculated to be at 1.20 wt%. As for MmNi5 at 313K abd 323K, the results are pointed at 0.9 wt% and 0.8 wt% whilst the plateau was encountedered at 20 and 24 bar, respectively. Study conducted on MmNi4.85Fe0.15 showed inconsistent findings with theory. After thorough examination, it was realized that the misbehavior of the sample was due to the insufficient agrresiveness activations method employed. Penerbit UTM Press 2001-12 Article PeerReviewed application/pdf en http://eprints.utm.my/1516/1/JT35F1.pdf Johari, Anwar and Mohd. Yunus, Rosli and Noordin, Mohd. Suffian and Md. Ghazali, Mohd. Nazlee Faisal and Tuan Abdullah, Tuan Amran (2001) MmNi5 and MmNi4.85Fe0.15 as Hydrogen Storage Medium. Jurnal Teknologi F (35F). pp. 1-10. ISSN 0127-9696 http://www.penerbit.utm.my/onlinejournal/35/F/JT35F1.pdf |
| spellingShingle | TP Chemical technology Johari, Anwar Mohd. Yunus, Rosli Noordin, Mohd. Suffian Md. Ghazali, Mohd. Nazlee Faisal Tuan Abdullah, Tuan Amran MmNi5 and MmNi4.85Fe0.15 as Hydrogen Storage Medium |
| title | MmNi5 and MmNi4.85Fe0.15 as Hydrogen Storage Medium |
| title_full | MmNi5 and MmNi4.85Fe0.15 as Hydrogen Storage Medium |
| title_fullStr | MmNi5 and MmNi4.85Fe0.15 as Hydrogen Storage Medium |
| title_full_unstemmed | MmNi5 and MmNi4.85Fe0.15 as Hydrogen Storage Medium |
| title_short | MmNi5 and MmNi4.85Fe0.15 as Hydrogen Storage Medium |
| title_sort | mmni5 and mmni4 85fe0 15 as hydrogen storage medium |
| topic | TP Chemical technology |
| url | http://eprints.utm.my/1516/1/JT35F1.pdf |
| work_keys_str_mv | AT joharianwar mmni5andmmni485fe015ashydrogenstoragemedium AT mohdyunusrosli mmni5andmmni485fe015ashydrogenstoragemedium AT noordinmohdsuffian mmni5andmmni485fe015ashydrogenstoragemedium AT mdghazalimohdnazleefaisal mmni5andmmni485fe015ashydrogenstoragemedium AT tuanabdullahtuanamran mmni5andmmni485fe015ashydrogenstoragemedium |