Optical properties of the TeO2-PbO-Li2O-Nd2O3 glass system
Nd-doped Tellurite glasses of the (80-x)TeO2-10PbO-10Li2O-xNd2O3 system, where x = 0.5, 1.0, 1.5, 2.0, 2.5 and 3.0 mol% have successfully been synthesized by melt-quenching techniques. Their absorption spectra had been characterized in the ranges of 400-900 nm while the luminescence spectra are meas...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
2008
|
| Subjects: | |
| Online Access: | http://eprints.utm.my/6729/1/rahimsahar-PAPER_optial_SPECTROSCOPY1.doc |
| _version_ | 1796854123250843648 |
|---|---|
| author | Sahar, M. R. Kassim, Azman Rohani, M. S. Ariffin, R. |
| author_facet | Sahar, M. R. Kassim, Azman Rohani, M. S. Ariffin, R. |
| author_sort | Sahar, M. R. |
| collection | ePrints |
| description | Nd-doped Tellurite glasses of the (80-x)TeO2-10PbO-10Li2O-xNd2O3 system, where x = 0.5, 1.0, 1.5, 2.0, 2.5 and 3.0 mol% have successfully been synthesized by melt-quenching techniques. Their absorption spectra had been characterized in the ranges of 400-900 nm while the luminescence spectra are measured in the range of 400 to 1500 nm. The experimental, and calculated, oscillator strength results are found to vary from 1.1566 x 10-6 to 0.8041 x 10-6 and from 1.0257 x 10-6 to 0.7715 x 10-6 with respect to the Nd3+content respectively. Meanwhile, the Judd-Ofelt parameters, varies from 3.472 x 1020cm2 to 2.576 x 1020cm2, varies from 2.110 x 1020cm2 to 2.108 x 1020cm2 and varies from 2.424 x 1020cm2 to 2.392 x 1020cm2 with respect to Nd3+ content. From the luminescence spectra it is observed that the emission occurs at 485nm, 560nm, 605nm, 880nm, 1062nm and 1340nm, which is due to 4G9/2 → 4I9/2, 2G9/2 → 4I11/2 , 2H11/2 → 4I9/2 , 4F3/2 → 4I9/2 , 4F3/2 → 4I11/2 and 4F3/2 → 4I13/2 transitions respectively. |
| first_indexed | 2024-03-05T18:09:41Z |
| format | Article |
| id | utm.eprints-6729 |
| institution | Universiti Teknologi Malaysia - ePrints |
| language | English |
| last_indexed | 2024-03-05T18:09:41Z |
| publishDate | 2008 |
| record_format | dspace |
| spelling | utm.eprints-67292017-09-07T03:44:46Z http://eprints.utm.my/6729/ Optical properties of the TeO2-PbO-Li2O-Nd2O3 glass system Sahar, M. R. Kassim, Azman Rohani, M. S. Ariffin, R. QC Physics Nd-doped Tellurite glasses of the (80-x)TeO2-10PbO-10Li2O-xNd2O3 system, where x = 0.5, 1.0, 1.5, 2.0, 2.5 and 3.0 mol% have successfully been synthesized by melt-quenching techniques. Their absorption spectra had been characterized in the ranges of 400-900 nm while the luminescence spectra are measured in the range of 400 to 1500 nm. The experimental, and calculated, oscillator strength results are found to vary from 1.1566 x 10-6 to 0.8041 x 10-6 and from 1.0257 x 10-6 to 0.7715 x 10-6 with respect to the Nd3+content respectively. Meanwhile, the Judd-Ofelt parameters, varies from 3.472 x 1020cm2 to 2.576 x 1020cm2, varies from 2.110 x 1020cm2 to 2.108 x 1020cm2 and varies from 2.424 x 1020cm2 to 2.392 x 1020cm2 with respect to Nd3+ content. From the luminescence spectra it is observed that the emission occurs at 485nm, 560nm, 605nm, 880nm, 1062nm and 1340nm, which is due to 4G9/2 → 4I9/2, 2G9/2 → 4I11/2 , 2H11/2 → 4I9/2 , 4F3/2 → 4I9/2 , 4F3/2 → 4I11/2 and 4F3/2 → 4I13/2 transitions respectively. 2008 Article NonPeerReviewed application/msword en http://eprints.utm.my/6729/1/rahimsahar-PAPER_optial_SPECTROSCOPY1.doc Sahar, M. R. and Kassim, Azman and Rohani, M. S. and Ariffin, R. (2008) Optical properties of the TeO2-PbO-Li2O-Nd2O3 glass system. - . (Unpublished) |
| spellingShingle | QC Physics Sahar, M. R. Kassim, Azman Rohani, M. S. Ariffin, R. Optical properties of the TeO2-PbO-Li2O-Nd2O3 glass system |
| title | Optical properties of the TeO2-PbO-Li2O-Nd2O3 glass system |
| title_full | Optical properties of the TeO2-PbO-Li2O-Nd2O3 glass system |
| title_fullStr | Optical properties of the TeO2-PbO-Li2O-Nd2O3 glass system |
| title_full_unstemmed | Optical properties of the TeO2-PbO-Li2O-Nd2O3 glass system |
| title_short | Optical properties of the TeO2-PbO-Li2O-Nd2O3 glass system |
| title_sort | optical properties of the teo2 pbo li2o nd2o3 glass system |
| topic | QC Physics |
| url | http://eprints.utm.my/6729/1/rahimsahar-PAPER_optial_SPECTROSCOPY1.doc |
| work_keys_str_mv | AT saharmr opticalpropertiesoftheteo2pboli2ond2o3glasssystem AT kassimazman opticalpropertiesoftheteo2pboli2ond2o3glasssystem AT rohanims opticalpropertiesoftheteo2pboli2ond2o3glasssystem AT ariffinr opticalpropertiesoftheteo2pboli2ond2o3glasssystem |