Characterization of defect induced multilayer graphene
A study of oxygen plasma on multilayer graphene is done with different flow rates. This is to allow a controlled amount of defect fabricated on the graphene. Results from the study showed that the intensity ratio of defect between D peak and G peak was strongly depended on the amount of oxygen flow...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Published: |
Institute of Advanced Engineering and Science
2017
|
| Subjects: |
| Summary: | A study of oxygen plasma on multilayer graphene is done with different flow rates. This is to allow a controlled amount of defect fabricated on the graphene. Results from the study showed that the intensity ratio of defect between D peak and G peak was strongly depended on the amount of oxygen flow rate thus affected the 2D band of the spectra. The inter-defect distance LD ≥ 15 nm of each sample indicated that low-defect density was fabricated. The surface roughness of the multilayer graphene also increased and reduced the conductivity of the multilayer graphene. |
|---|