Highly crystalline zinc oxide/mesoporous hollow silica composites synthesized at low temperature for the photocatalytic degradation of sodium dodecylbenzenesulfonate
Highly crystalline ZnO/mesoporous hollow silica sphere (MHSS) composites have been successfully synthesized through an impregnation method at 323 K without applying calcination. Three composites of different Zn/Si molar ratios of 1: 2, 1: 1, and 2: 1 were prepared. X-Ray diffraction patterns confirm...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Published: |
CSIRO
2019
|
| Subjects: |
| Summary: | Highly crystalline ZnO/mesoporous hollow silica sphere (MHSS) composites have been successfully synthesized through an impregnation method at 323 K without applying calcination. Three composites of different Zn/Si molar ratios of 1: 2, 1: 1, and 2: 1 were prepared. X-Ray diffraction patterns confirmed the presence of highly crystalline ZnO in the materials. A layer of ZnO was formed on the MHSS as evidenced by field emission scanning electron microscopy analysis. Transmission electron microscopy analysis verified the mesoporous structure in ZnO/MHSS composites. N 2 adsorption-desorption analysis indicated a type IV isotherm for 1ZnO/2MHSS and 1ZnO/1MHSS samples, confirming the presence of mesopores in the ZnO layer. It has been demonstrated that all the ZnO/MHSS composites exhibit a high photocatalytic activity towards sodium dodecylbenzenesulfonate degradation compared with bare ZnO under UV irradiation. A kinetic study showed that the photodegradation followed a second order model. Among the prepared composites, 1ZnO/1MHSS recorded the highest reaction rate of 6.03 × 10 -3 mM -1 min -1 which is attributed to a high crystallinity and the monodispersity of a high amount of ZnO on MHSS. |
|---|