Study on the properties of palm oil fiber
This study investigated the strength and durability of Palm Oil Fiber Reinforced Concrete (POFRC). Two POFRC mixes with two different content and length of palm oil fiber (POF) were used. Specimen PF1 contained 0.50% POF of 3 cm length while specimen PF2 contained 0.25% POF of 5 cm length. The stren...
| Main Author: | |
|---|---|
| Format: | Monograph |
| Language: | English |
| Published: |
Faculty of Civil Engineering
2009
|
| Subjects: | |
| Online Access: | http://eprints.utm.my/9735/1/78238.pdf |
| _version_ | 1825910369286094848 |
|---|---|
| author | El-Gelany Ismail, Mohamed Abdelkader |
| author_facet | El-Gelany Ismail, Mohamed Abdelkader |
| author_sort | El-Gelany Ismail, Mohamed Abdelkader |
| collection | ePrints |
| description | This study investigated the strength and durability of Palm Oil Fiber Reinforced Concrete (POFRC). Two POFRC mixes with two different content and length of palm oil fiber (POF) were used. Specimen PF1 contained 0.50% POF of 3 cm length while specimen PF2 contained 0.25% POF of 5 cm length. The strength and durability of both specimens were compared with a control mix, P0. The concrete specimens were cured in water for 28 days, before immersing them in 1% hydrochloric acid solution for 1800 hours. The durability of POFRC against acid attack was evaluated by the loss of weight and compressive strength. In this paper, the attack of chloride ions on specimens immersed in 3% sodium chloride solution using the colorimetric method was studied. After 7, 28 and 90 days curing, the progressive deterioration was evaluated through spraying of 0.2N silver nitrate solution on the split cylinders and by visual inspection. Microanalyses were conducted upon test termination to elucidate the damage mechanisms using FESEM and EDX analysis. In most cases, PF1, which had the highest fiber content (0.5%) did not give good results while PF2 showed good performance against deteriorations compared to the control mix, P0. |
| first_indexed | 2024-03-05T18:16:02Z |
| format | Monograph |
| id | utm.eprints-9735 |
| institution | Universiti Teknologi Malaysia - ePrints |
| language | English |
| last_indexed | 2024-03-05T18:16:02Z |
| publishDate | 2009 |
| publisher | Faculty of Civil Engineering |
| record_format | dspace |
| spelling | utm.eprints-97352011-05-18T10:07:00Z http://eprints.utm.my/9735/ Study on the properties of palm oil fiber El-Gelany Ismail, Mohamed Abdelkader TA Engineering (General). Civil engineering (General) This study investigated the strength and durability of Palm Oil Fiber Reinforced Concrete (POFRC). Two POFRC mixes with two different content and length of palm oil fiber (POF) were used. Specimen PF1 contained 0.50% POF of 3 cm length while specimen PF2 contained 0.25% POF of 5 cm length. The strength and durability of both specimens were compared with a control mix, P0. The concrete specimens were cured in water for 28 days, before immersing them in 1% hydrochloric acid solution for 1800 hours. The durability of POFRC against acid attack was evaluated by the loss of weight and compressive strength. In this paper, the attack of chloride ions on specimens immersed in 3% sodium chloride solution using the colorimetric method was studied. After 7, 28 and 90 days curing, the progressive deterioration was evaluated through spraying of 0.2N silver nitrate solution on the split cylinders and by visual inspection. Microanalyses were conducted upon test termination to elucidate the damage mechanisms using FESEM and EDX analysis. In most cases, PF1, which had the highest fiber content (0.5%) did not give good results while PF2 showed good performance against deteriorations compared to the control mix, P0. Faculty of Civil Engineering 2009-09-14 Monograph NonPeerReviewed application/pdf en http://eprints.utm.my/9735/1/78238.pdf El-Gelany Ismail, Mohamed Abdelkader (2009) Study on the properties of palm oil fiber. Project Report. Faculty of Civil Engineering, Skudai, Johor. (Unpublished) |
| spellingShingle | TA Engineering (General). Civil engineering (General) El-Gelany Ismail, Mohamed Abdelkader Study on the properties of palm oil fiber |
| title | Study on the properties of palm oil fiber |
| title_full | Study on the properties of palm oil fiber |
| title_fullStr | Study on the properties of palm oil fiber |
| title_full_unstemmed | Study on the properties of palm oil fiber |
| title_short | Study on the properties of palm oil fiber |
| title_sort | study on the properties of palm oil fiber |
| topic | TA Engineering (General). Civil engineering (General) |
| url | http://eprints.utm.my/9735/1/78238.pdf |
| work_keys_str_mv | AT elgelanyismailmohamedabdelkader studyonthepropertiesofpalmoilfiber |