Glass formation and elastic behavior of bismuth borate glass system
Published 2007“…Bismuth borate glass is of great interest in optoelectronic devices due to its low melting temperature (600–800 °C), extensive glass formation range, high refractive index ranging from 1.9 to 2.3, high physical and chemical stability, and nonlinear optical property. …”
Get full text
Conference or Workshop Item -
2
Ciri Kenyal dan Rawat Haba Bagi Kaca Argentum Borat dan Fosfat
Published 2001“…Dalam kajian ini, kaca argentum dengan pembentuk kaca borat dan fosfat telah dikaji. Empat siri kaca telah berjaya disintisiskan iaitu argentum borat (Ag20)x (B203)J-x (x = 0.2 hingga 0.4), argentum iodida (P205)I-x (x = 0.2 hingga 0.5) dan argentum iodida fosfat (AgI)x [Ag20 2 P205]I-X (x = 0.035 hingga 0.6). …”
Get full text
Thesis -
3
-
4
-
5
-
6
A comparative study of the experimental and the theoretical elastic data of Tm3+ doped zinc borotellurite glass
Published 2017“…It was found that the addition of thulium caused bridging and non-bridging oxygen to be formed at the same time due to the different effect that occur to tellurite and borate network as thulium is added. As thulium is varied from 1 until 3 mol%, bridging oxygens had been found to occur at a high rate and caused the ultrasonic velocity to increase. …”
Get full text
Article -
7
A comparative study of the experimental and the theoretical elastic data of Tm3þ doped zinc borotellurite glass
Published 2017“…It was found that the addition of thulium caused bridging and non-bridging oxygen to be formed at the same time due to the different effect that occur to tellurite and borate network as thulium is added. As thulium is varied from 1 until 3 mol%, bridging oxygens had been found to occur at a high rate and caused the ultrasonic velocity to increase. …”
Get full text
Article -
8
Preparation and elastic moduli of germanate glass containing lead and bismuth
Published 2012“…The current experimental data are compared with those of bismuth lead borate (B2O3)20–(PbO)80−x–(Bi2O3)x. The elastic properties of BPG were studied using the ultrasonic pulse-echo technique where both longitudinal and transverse sound wave velocities have been measured in each glass samples at a frequency of 15 MHz and at room temperature. …”
Get full text
Article