1
Corrosion behaviour of heat threated carbon steel
Published 2012“…A standard micro hardness tester, equipped with a Vickers indenter and an indentation load of 500 gf was used for surface hardness measurement. …”
Get full text
Undergraduates Project Papers -
2
Investigation of mechanical properties of aluminium-steel welding using different welding technique and processes
Published 2013“…The experiments carried out along this research such as non-destructive test (NDT), Vickers hardness test, tensile test and microstructure optical analysis. …”
Get full text
Undergraduates Project Papers -
3
Investigation of surface modification on aluminum oxide using acid etching surface pretreatment
Published 2012“…In addition, the micro hardness test indicated that average Vickers micro hardness of alumina as-received specimen was 1202.47 HV while coated alumina with acid etching pre-treatment specimen was 2293.43 HV. …”
Get full text
Undergraduates Project Papers -
4
Investigation of machining performance of the coated carbide cutting tools with acid etching surface pretreatment
Published 2012“…In addition, the hardness test indicated that average Vickers hardness of original tungsten carbide specimen was 970.7 HV while coated tungsten carbide with acid etching pretreatment specimen was 1232.33 HV. …”
Get full text
Undergraduates Project Papers -
5
Evaluation of nickel electroless plating on mild steel
Published 2010“…Then the surface structure and morphology nickel plating was evaluated using scanning electron microscopy (SEM), Optical Microscope while its hardness was evaluated using Vickers hardness test. In electroless plating, anode is the movements of negative ions toward the positive electrode and the mild steel as the cathode because the movement of positive ions toward the negative electrode. …”
Get full text
Undergraduates Project Papers -
6
Study the microstructure and mechanical properties of nickel-aluminium intermetallic alloy
Published 2017“…Microstructural evolution and the relationship between microstructure and mechanical properties of different composition Ni-Al intermetallic alloy were investigated by using X-ray diffraction, scanning electron microscopy, Vickers hardness and direct measurement of density. …”
Get full text
Get full text
Get full text
Get full text
Undergraduates Project Papers -
7
Fatigue analysis of similar and dissimilar solid rod welding using friction welding process
Published 2013“…For the mechanical properties, fatigue test was conducted to analyze the strength and Vickers hardness test to determine the hardness at the weld joint area. …”
Get full text
Get full text
Get full text
Get full text
Undergraduates Project Papers -
8
Surface integrity of titanium when machining with various cutting parameter
Published 2010“…The surface roughness of the bar will be measured by using perthometer Surfcom 130A and chip hardness will be measure by using Micro Vickers Hardness test. The data is analyzed in STATISTICA and manually plot in excel.…”
Get full text
Undergraduates Project Papers -
9
Development of ceramics cutting tool for machining using aluminium oxide reinforced with copper powder
Published 2016“…The result showed that 90% of the theoretical density was achieved and 70% by weight mixed with 30% copper was measured for the higher Vickers hardness value.…”
Get full text
Undergraduates Project Papers -
10
Investigation of machining performance of the PVD coated tungsten carbide by sandblasting pre-treatment
Published 2012“…In addition, the micro hardness test indicated that average Vickers micro hardness of original tungsten carbide specimen was 863.433 HV while coated carbide with sandblasting pre-treatment specimen was 1464.9 HV. …”
Get full text
Get full text
Get full text
Get full text
Undergraduates Project Papers -
11
Effect of aging on machinability of 6061 aluminium alloy
Published 2010“…The process that has been gone through the experiment are sample preparation, solution heat treated, aging at various times and temperatures, milling process, surface analysis, surface roughness and the Vickers hardness test. From the experiment, the sample is harder after gone through all the process. …”
Get full text
Undergraduates Project Papers -
12
Laser surface modification of AISI 1025 steel
Published 2013“…Hardness test were carried out by using Vickers indenter with Hv0.1. Optica microscope was used to study the depth of treated sample for metallographic study. …”
Get full text
Undergraduates Project Papers -
13
Effect of heat treatment on the corrosion resistance of aluminium alloys
Published 2010“…The microstructures of heat treated specimens have been observed using metallurgical microscope and scanning electron microscope while the hardness test has been done using Vickers hardness tester. The corrosion rates of the heat treated specimens were determined using weight loss method. …”
Get full text
Undergraduates Project Papers -
14
Effect of corrosion on aluminium tailor welded blanks (similar material welding)
Published 2013“…Tensile properties of welded joint were investigated by tensile test and hardness of the FZ, HAZ and BM was obtained by Vickers hardness test. From the corrosion test result, it shows that specimen weld by filler ER 4047 has good corrosion resistance than specimen weld by filler ER 4043. …”
Get full text
Undergraduates Project Papers -
15
The effects of pin profile on joining aluminium alloy by using friction stir welding technique
Published 2013“…Microstructural analysis was done by using optical microscope while Vickers hardness tests and tensile test was conducted to analyze the mechanical properties of weld joint. …”
Get full text
Undergraduates Project Papers -
16
The effects of single-pass/double-pass technique on friction stir welding of aluminium
Published 2013“…All the specimens were tested by using tensile test and Vickers hardness test to evaluate its mechanical properties. …”
Get full text
Undergraduates Project Papers -
17
An evaluation of Ni-Alumina composite electroplating on mild steel
Published 2010“…Lastly, all the samples were undergoes Vickers hardness test. In this project, it can be conclude that result shows increase of Alumina concentration, plating time, and voltage supplied also increase the thickness of coating.…”
Get full text
Undergraduates Project Papers -
18
Investigation of corrosion effects on aluminum-stainless steel weld joint
Published 2012“…Microstructure of welded area was studied using metallurgy microscope, mechanical properties observed by Vickers hardness and corrosion rate determined in artificial corrosion test with seawater aqueous solution. …”
Get full text
Undergraduates Project Papers -
19
Effect of reinforcement volume fraction on the mechanical properties of the al-sic composite
Published 2016“…The hardness was measured by the Vickers micro hardness testing machine as per the ASTM e348. …”
Get full text
Undergraduates Project Papers -
20
Investigation of wear behavior of cutting tool insert for ti-alloy machining using carbon coated with sic sandblasting and hf acid pretreatment
Published 2012“…The substrate surface after coating by different surface pretreatment was measured using Vickers Hardness machine. From the morphological observation, the as-received micrograph has a continuous 45° direction from the horizontal line. …”
Get full text
Undergraduates Project Papers