Effect of Strain Range on the Low Cycle Fatigue in  Alloy 617 at High Temperature

Effect of Strain Range on the Low Cycle Fatigue in  Alloy 617 at High Temperature

The aim of this study is to investigate the fully‐reversed low cycle fatigue properties of  Alloy 617 in the air at 950 °C; these tests were conducted at total strain ranges from 0.9% to 1.5%  with a constant strain rate of 10−3/s. The result of the fatigue tests showed a decrease in fatigue  resist...