Silicon carbide hot pressing sintered by magnesium additive: microstructure and sintering mechanism
Silicon carbide was hot pressing sintered at 1300 ̊C/30 MPa by using magnesium additive. Microstructure and sintering mechanism are studied. Result shows that the hot pressing sintered sample composed of both α-SiC and β-SiC, indicating that no polytype transition has happened. Magnesium with stacki...