Half-Heusler phase TmNiSb under pressure: intrinsic phase separation, thermoelectric performance and structural transition
Abstract Half-Heusler (HH) phase TmNiSb was obtained by arc-melting combined with high-pressure high-temperature sintering in conditions: p = 5.5 GPa, $$T_{HPHT}$$ T HPHT = 20, 250, 500, 750, and 1000 $$^{\circ }$$ ∘ C. Within pressing temperatures 20–750 $$^{\circ }$$ ∘ C the samples maintained H...