Secondary dendritic arm spacing and cooling rate relationship for an ASTM F75 alloy
The solidification evolution of an ASTM F75 alloy was studied for samples quenched during directional cooling. These samples were obtained using five extraction rates (1.2–18 mm/min) and two temperature gradients (6 and 12 K/mm), leading to a 25-fold change in the cooling rate (0.13–3.31 K/s). The s...