Microstructural Evolution in a 0.09% Niobium Low Carbon Steel during Controlled Hot Deformation
A series of plane strain compression tests were carried out in order to simulate the thermomechanical controlled processing of a 0.09wt% Nb low carbon steel, in a scheme of multipass finish rolling at 950 °C with interpass times of 10 s. It was observed that after the first two finishing passes a re...