Thickness-dependent piezoelectric behaviour and dielectric properties of lanthanum modified BiFeO3 thin films
Bi0.85La0.15FeO3 (BLFO) thin films were deposited on Pt(111)/Ti/SiO2 /Si substrates by the soft chemical method. Films with thicknesses ranging from 140 to 280 nm were grown on platinum coated silicon substrates at 500°C for 2 hours. The X-ray diffraction analysis of BLFO films evidenced a hexagonal...
Main Authors: | Glenda Biasotto, Francisco Moura, Cesar Foschini, Elson Longo, Jose A. Varela, Alexandre Z. Simões |
---|---|
Format: | Article |
Language: | English |
Published: |
University of Novi Sad
2011-03-01
|
Series: | Processing and Application of Ceramics |
Subjects: | |
Online Access: | http://www.tf.uns.ac.rs/publikacije/PAC/pdf/PAC%2011%2005.pdf |
Similar Items
-
Piezoelectric BiFeO<sub>3</sub> Thin Films: Optimization of MOCVD Process on Si
by: Quentin Micard, et al.
Published: (2020-03-01) -
Strain-driven phase transitions and associated dielectric/piezoelectric
anomalies in BiFeO3 thin films
by: Huang, Chuanwei, et al.
Published: (2011) -
Ferroelectric BiFeO3 thin-film optical modulators
by: Zhu, Minmin, et al.
Published: (2016) -
Review of Piezoelectric Properties and Power Output of PVDF and Copolymer-Based Piezoelectric Nanogenerators
by: Neelesh Bhadwal, et al.
Published: (2023-12-01) -
Review of Zinc Oxide Piezoelectric Nanogenerators: Piezoelectric Properties, Composite Structures and Power Output
by: Neelesh Bhadwal, et al.
Published: (2023-04-01)