Two Types of Wear Mechanisms Governing Transition between Mild and Severe Wear in Ti-6Al-4V Alloy during Dry Sliding at Temperatures of 20–250 °C

Two Types of Wear Mechanisms Governing Transition between Mild and Severe Wear in Ti-6Al-4V Alloy during Dry Sliding at Temperatures of 20–250 °C

Dry wear characteristics and wear mechanisms governing mild-severe wear transition of Ti-6Al-4V alloy were studied during sliding against medium carbon chromium steel (50Cr) in an experimental temperature range of 20–250 °C. At each experimental temperature, wear rate was plotted against applied loa...