Effect of irradiation temperature on the nanoindentation behavior of P92 steel with thermomechanical treatment
The nanoindentation behavior of P92 steel with thermomechanical treatment under 3.5 MeV Fe13+ ion irradiation at room temperature, 400 and 700 °C was investigated. Pop-in behavior is observed for all the samples with and without irradiation at room temperature, while the temperature dependence of po...