The precipitation behavior of MgZn2 and Mg4Zn7 phase in Mg-6Zn (wt.%) alloy during equal-channel angular pressing
As-extruded Mg-6Zn (wt.%) Alloy was subjected to severe plastic deformation (SPD) by the equal-channel angular pressing(ECAP) at 160 oC. The results of tensile tests at room temperature showed that two passes ECAP resulted in a remarkable improvement of strength, yield strength from 200 to 265 MPa a...