Criteria of Activation of Powdery Materials by a Preliminary Mechanical Treatment
γ-Fe2O3 was vibration ball-milled with varying amplitude, α, from 8 to 24mm and grinding time. The enthalpy increase, ΔH*, due to mechanical treatment was measured by a differential scanning calorimeter. Pretreated sample was subsequently heated at 693K for 60min, and the fractional transformation i...