Microstructure and tempering softening mechanism of modified H13 steel with the addition of Tungsten, Molybdenum, and lowering of Chromium
The rapid development in the advanced manufacturing industry asks for better tempering softening resistance (TSR) of Hot work die steels. In this work, a modified H13 steel (CXN03 steel) with additional tungsten, molybdenum, and lowering chromium was prepared. The TSR of CXN03 is significantly bette...