Microstructure and tempering softening mechanism of modified H13 steel with the addition of Tungsten, Molybdenum, and lowering of Chromium
The rapid development in the advanced manufacturing industry asks for better tempering softening resistance (TSR) of Hot work die steels. In this work, a modified H13 steel (CXN03 steel) with additional tungsten, molybdenum, and lowering chromium was prepared. The TSR of CXN03 is significantly bette...
Main Authors: | Hengnan Ding, Tian Liu, Jiabo Wei, Leli Chen, Fuyang Cao, Baosen Zhang, Rui Luo, Xiaonong Cheng |
---|---|
Format: | Article |
Language: | English |
Published: |
Elsevier
2022-12-01
|
Series: | Materials & Design |
Subjects: | |
Online Access: | http://www.sciencedirect.com/science/article/pii/S026412752200939X |
Similar Items
-
Study on the Softening Behavior of Cu–Cr–In Alloy during Annealing
by: Yunqing Zhu, et al.
Published: (2020-04-01) -
Dynamic Softening and Hardening Behavior and the Micro-Mechanism of a TC31 High Temperature Titanium Alloy Sheet within Hot Deformation
by: Kexin Dang, et al.
Published: (2021-10-01) -
On the Measurability and Predictability of HAZ Softening in GMAW of Automotive DP980 Steel
by: Cecilio J. Martínez-González, et al.
Published: (2022-06-01) -
Dynamic Softening Mechanisms and Microstructure Evolution of TB18 Titanium Alloy during Uniaxial Hot Deformation
by: Qiang Fu, et al.
Published: (2021-05-01) -
The comparison of gas tungsten arc welding and flux cored arc welding effects on dual phase steel
by: Mahmoud Abbas, et al.
Published: (2020-01-01)