Influence of Preaging Temperature on the Indentation Strength of 3Y-TZP Aged in Ambient Atmosphere
Yttria-stabilized zirconia (3Y-TZP) containing 0.25% Al<sub>2</sub>O<sub>3</sub>, which is resistant to low temperature degradation (LTD), was aged for 10 h at 130–220 °C in air. The aged specimens were subsequently indented at loads ranging from 9.8 to 490 N using a Vickers...